Thermal stability of stoichiometric strontium-incorporated hydroxyapatite

Dagang Guo,Kewei Xu,Yong Han

DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.03.011

2006-01-01

Rare Metal Materials and Engineering

Abstract:Several stoichiometric strontium-incorporated hydroxyapatite powders with different content of strontium ion in place of calcium ion have been investigated on their thermal stabilities, including phase structure, chemical composition and crystal size and morphology at different temperatures. Results show that there exists a competition between phase decomposition and crystal growth of apatite. With the firing temperature climbing to 1300 degrees C, no change happens to phase component of pure HAP, but the crystal apparently grows from 20 nm similar to 40 nm at 600 degrees C to similar to 20 mu m at 1300 degrees C. However, after some Sr2+ incorporating into hydroxyapatite crystal by replacing equivalent Ca2+, the larger ion radius and the inhibiting action on growth of apatite of Sr2+ make the decomposition of Sr-incorporated hydroxyapatite (Sr-HAP) prior to its crystal growth. Thus, Sr-HAP starts to decompose into tricalcium phosphate at 900 degrees C, which becomes serious at a higher firing temperature and more incorporation of Sr2+. Although the crystal further grows up when increasing the firing temperature, the range of growth is much lower than that of pure HAP. At 13001 degrees C, Sr-HAP also maintains a similar equiaxial crystal (440 nm similar to 730 nm x 220 nm similar to 370 nm).