Abstract:Biocompatible hydroxyapatite (HAp) powders have thermodynamically driven tendencies to lower their surface areas due to the formation of irreversible aggregates. To address this challenge, HAp hybrid powders are herein prepared by using a traditional wet-precipitation method with subsequent hydrothermal carbonization for surface modification. The crystallite size, crystallite degree and area ratio of the infrared peak assigned to bonding water against those of free water are determined to investigate the variation of HAp crystallization with processing parameters. The crystallization of HAp is facilitated by enriched water in a stealth layer with water molecules evolved by citrate, nitrogen (N)-containing methylene blue (MB), hydrogen-group-rich β-cyclodextrin (CD) and oxygen-containing organic carbon shells. The low surface areas result in fabrication of nano-sized HAp powders with a uniform size distribution, well-dispersed morphologies and smooth surfaces through calcination of HAp-CD-MB@C. The pH values of acidic buffers increase slowly during incubation of HAp-CD-MB@C powders with chemical stability and a large grain size after calcination at 550°C for 2 h. The present study will shed light on the preparation of nano-sized inorganic powders with a uniform size distribution, well-dispersed morphologies and modulated chemical stability for potential applications as carriers of small molecular substances and fillers in composite materials.

Preparation and thermal stability analysis of hydroxyapatite derived from the precipitation process and microwave irradiation method

Hydrothermal synthesis of nano-hydroxyapatite crystals

Preparation of nanorod hydroxyapatite by combination of chemical precipitation and microwave technique

Effect of Heating Mode on Thermal Stability of Nanocrystalline Hydroxyapatite

Preparation of Calcium-Deficient Carbonated Nanohydroxyapatite by Microwave Process

Effect of Ultrasonic Wave and Heat Treatment on the Crystallinity and Morphology of Hydroxyapatite

High-Temperature Characteristics of Synthetic Hydroxyapatite

Effect of Ca/P Molar Ratio and Heat Treatment on Thermal Decomposition and Reconstitution of Hydroxyapatite

Calcined Hydroxyapatite Powders with Increased Chemical Stabilities and Dispersibility

Preparation of hydroxyapatite nanopowders by using Ca(NO3)(2)-P2O5 ethanol solution system

Preparation of High Quality Nano-hydroxyapatite Powder by Coprecipitation Method

Preparation of Calcium-Deficient Carbonated Hydroxyapatite Nanoparticles by Microwave Process

Synthesis of Nanosized Carbonated Hydroxyapatite under Microwave Irradiation

Preparation and crystallization control of nanoparticle hydroxyapatite

Effects of Temperature and Concentration on the Nano-Sized Hydroxyapatite Whisker Prepared by Chemical Precipitation Method

Thermal Stability of Hydroxyapatite Whiskers Prepared by Homogenous Precipitation

Influence of Dispersant and Heat Treatment on the Morphology of Nanocrystalline Hydroxyapatite

Increased chemical stabilities of well-dispersed hydroxyapatite (HAp) powders prepared by calcination of HAp-β-cyclodextrin-methylene blue@carbon

Preparation of Nano Hydroxyapatite by Coprecipitation

Effect of the Heating Time on the Preferred Growth of Hydroxyapatite Crystal Prepared by Microwave-Hydrothermal Technique on the Defective Surface of Sprayed Coating

Preparation of Porous Spherical Hydroxyapatite Particles by Phosphoration of Calcium Carbonate