Abstract:Bulk amorphous alloys in a cylindrical form wire prepared in the diameter range up to about 5 mm for Zr65Al7.5Ni10Cu17.5-xAgx (x=0 to 5 at%) by copper mold casting. These bulk amorphous alloys exhibit a wide supercooled liquid region before crystallization and the temperature interval defined by the difference between glass transition temperature (T-g) and crystallization temperature (T-x), Delta T-x(=T-x-T-g) is 111 K for the 0%Ag alloy and 63 K for the 5%Ag alloy. The replacement of Cu by 5 at%Ag causes the change in the crystallization process from a single stage of Am-->Zr-2(Cu, Ni) + Zr-2(Al, Ni) to two stages of Am-->Am' + Zr-3(Al, Ag)(2)-->Zr-3(Al, Ag)(2) + Zr-2(Cu, Ni). The Zr-3(Al, Ag)(2) phase has a spherical shape with a small size of about 20 nm and is dispersed homogeneously at an interparticle spacing of about 30 nm. The change in the crystallization process by the addition of Ag is presumably due to the generation of the distinction of bonding nature among the constituent elements because of the positive heats of mixing for Ag-Ni and Ag-Cu pairs. The dispersion of the nanoscale Zr-3(Al, Ag)(2) phase causes a significant increase in tensile fracture strength (sigma(f)) from 1150 MPa for the amorphous single phase to 1520 MPa for the amorphous phase containing about 14% volume fraction of Zr-3(Al, Ag)(2) phase. The shear-type fracture mode along the maximum shear plane remains unchanged. The effectiveness of the Zr-3(Al, Ag)(2) phase for the increase in sigma(f) is presumably because the size of the phase is too small to contain dislocations. The success of synthesizing the high-strength bulk amorphous alloy consisting of nanoscale Zr-3(Al, Ag)(2) phase embedded in an amorphous matrix is encouraging for future development of bulk amorphous alloys as a high-strength material.

Nanocrystalline formation in Zr52.5Cu27Ni5.5 Al22Nb3 amorphous alloy and the effect on compress mechanical properties

Nanocrystal composites in Zr–Nb–Cu–Al metallic glasses

Ultrasonic excitation induced nanocrystallization and toughening of Zr<sub>46.75</sub>Cu<sub>46.75</sub>Al<sub>6.5</sub> bulk metallic glass

Thermal and Mechanical Properties of Amorphous Zr65Al7.5Ni10Cu12.5Ag5 Alloy Containing Nanocrystalline Compound Particles

Deformation behavior of Zr-based bulk nanocrystalline amorphous alloys

Nanocrystalline Composites with High Strength Obtained in Zr–Ti–Ni–Cu–Al Bulk Amorphous Alloys

Effect of Sn and Al Additions on the Microstructure and Mechanical Properties of Amorphous Ti–Cu–Zr–Ni Alloys

Mechanical Properties of Bulk Amorphous Zr-Al-Cu-Ni-Ag Alloys Containing Nanoscale Quasicrystalline Particles

Microstructures and Tensile Properties of CuZrAlNb Metallic Glass Composites under Different Cooling Rates

Preparation And Thermal Stability Of Zr-Al-Ni-Cu-Nb Bulk Amorphous Alloy Matrix Composites

Microstructure Evolution and Mechanical Properties of Nb-alloyed Cu-based Bulk Metallic Glasses and Composites

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Effect of Nb Addition on Thermal Stability, Glass Forming Ability and Mechanical Properties of Zr-Based Bulk Amorphous Alloys

Preparation Of Bulky Amorphous Zr-Al-Co-Ni-Cu Alloys By Copper Mold Casting And Their Thermal And Mechanical-Properties

Room-Temperature Mechanical Characterization of Bulk Glassy and Partially Crystallized Zr63Al9.7Ni9.7Cu14.6Nb3 Alloys

Room-Temperature Mechanical Characterization of Bulk Glassy and Partially Crystallized Zr<sub>63</sub>Al<sub>9.7</sub>Ni<sub>9.7</sub>Cu<sub>14.6</sub>Nb<sub>3</sub> Alloys

Effect of isothermal annealing on hardness and elastic modulus of ZrCuAlNiCoNb amorphous alloys

Enhanced Ductility in a Zr65Cu15Al10Ni10 Bulk Metallic Glass by Nanocrystallization During Compression

Glass Forming Ability and Mechanical Properties of Cu-Zr-Al-Nb Amorphous Alloy

Static mechanical characterization of a bulk amorphous and nanocrystalline Zr40Ti14Ni11Cu10Be25 alloy

Synthesis of High Strength Bulk Amorphous Zr–Al–Ni–Cu–Ag Alloys with a Nanoscale Secondary Phase