Effect of Substituted Positions of Acetylene Groups in Benzene Rings on the Properties of Poly(silane Arylether Arylacetylene)s
Jixian Li,Changjun Gong,Junkun Tang,Qiaolong Yuan,Zuozhen Liu,Farong Huang
DOI: https://doi.org/10.1038/s41428-023-00819-z
IF: 3.135
2023-01-01
Polymer Journal
Abstract:Performing investigations on the structure-property relationship of poly(silane arylether arylacetylene)s (PSEAs) is very important and instructive for designing novel high-performance polymers. In this work, three bifunctional acetylene-terminated triphenyl-ether monomers with either para -acetylene, meta -acetylene or ortho -acetylene, i.e., 1,3-bis(4'-ethynylphenoxy)benzene ( pmp -BEPB), 1,3-bis(3'-ethynylphenoxy)benzene ( mmm -BEPB) and 1,3-bis(2'-ethynylphenoxy)benzene ( omo -BEPB) were synthesized and used to prepare three PSEA resins, namely, pmp -PSEA, mmm -PSEA and omo -PSEA. The PSEA resins were characterized by 1 H-nuclear magnetic resonance spectroscopy, Fourier transform infrared spectroscopy and X-ray diffraction analysis, and the properties were explored. The resins possess a wide processing window in the following order: pmp -PSEA < mmm -PSEA < omo -PSEA. The DSC results revealed that pmp -PSEA shows the highest reactivity, followed by omo -PSEA and mmm -PSEA. In the cured networks of the resins, the densities increase in the following order: pmp -PSEA-C < mmm -PSEA-C < omo -PSEA-C. Compared with pmp -PSEA-C, mmm -PSEA-C possesses better mechanical properties with a flexural strength of 66.5 MPa and a flexural modulus of 3.71 GPa. The decomposition temperatures of 5% weight loss ( T d5 ) of pmp -PSEA-C and mmm -PSEA-C are over 530 °C.