Nanocrystalline Structures of Fe-Ni-P-B Alloy Solidified at Large Undercooling and Liquid Spinonal Decomposition

Zhang Changqing,Yao Kefu

IF: 1.797

2006-01-01

ACTA METALLURGICA SINICA

Abstract:The undercooling of Fe40Ni40P14B6 alloy melt can be enhanced greatly by using fluxing purification technique. The solidification structures of the alloy under different undercoolings are quite difference and with increasing undercooling the microstructure was refined significantly. When the undercooling is large enough, nanosize solidification structure can be obtained. In present work, at the undercooling of 360 K, the as-prepared bulk nanocrystalline alloy possesses the average grain size of 40 nm. It has been found that the alloy melt will experience Spinodal decomposition, resulting in the appearance of the network characteristics in solidified structure if the undercooling is large enough. The thermodynamics analysis results indicate that the characteristic sizes of the network structure resulted by Spinodal decomposition are close related to the undercooling of the alloy melt, the larger the undercooling, the smaller the grain size.