Abstract:This research aims to increase the activity of platinum–ruthenium alloy (PtRu/C) catalysts for methanol electrooxidation. The direct methanol fuel cell (DMFC) anodic PtRu/C catalysts were prepared from acidic and alkaline Pt(NH3)2(NO2)2 solutions as Pt precursors, respectively, and with the same acidic Ru compound but without Cl− ion as the Ru precursor by thermal reduction. The phase structures, lattice parameters, particle sizes, alloy composition, distribution, and the morphology of reduced catalysts were determined by means of X-ray diffraction (XRD), energy-dispersive analysis of X-ray (EDAX), and high-resolution transmission electron microscopy (TEM). It was found that the XRD patterns of the two catalysts showed Pt reflections for a face centered cubic (fcc) crystalline alloy structure. The catalyst prepared from the acidic Pt(NH3)2(NO2)2 as a precursor has a more homogeneous distribution of PtRu metal particles on carbon. Its size is relatively small, about 3.7nm. Its chemical composition is quite similar to theoretical value of 1:1 (Pt:Ru). The catalyst prepared from the alkaline Pt(NH3)2(NO2)2 as a precursor has an uneven distribution of PtRu particles on carbon and its size is relatively large, and the chemical composition of Pt and Ru was 6:4. The performance was tested using a glassy carbon working electrode by cyclic voltammetry (CV) and chronoamperometric curves in a solution of 0.5molL−1 CH3OH and 0.5molL−1 H2SO4 at 25°C. The electrocatalytic activity of the PtRu/C catalyst prepared from the acidic Pt(NH3)2(NO2)2 as a precursor was the higher for methanol electrooxidation than that of catalyst from the alkaline source. The peak current density from the CV plot was 11.5mAcm−2.

Effects of the precursors on the performance of Pt/C nano -catalysts

Effect of precursors on carbon supported platinum nano-catalyst

Preparation and Performance of Ni Nano-particle Doping with Pt for Methanol Electrocatalytic Oxidation

The Influence of Three Groups of Pt-Ru/C Catalyst’s Precursors on Its Performance for Direct Methanol Fuel Cell

Preparation and Application in Assembling High-Performance Fuel Cell Catalysts of Colloidal PtCu Alloy Nanoclusters

Effect of PVP on the Dispersity of Pt Nanoparticles and Catalytic Activity in Synthesis of Pt/C Catalysts for Fuel Cell

The influence of acidic and alkaline precursors on Pt{single bond}Ru/C catalyst performance for a direct methanol fuel cell

Influences of Pd precursors and preparation method on the catalytic performances of Pd-only close-coupled catalysts

New Pt—Ru Solid Compounds As Precursors of Anodic Catalysts for Direct Methanol Fuel Cell.

Preparation and characterization of Pt/C cathode catalysts for direct methanol fuel cells effect of different preparation and treatment methods

Preparation and Performance of Anode Catalysts Pt/C for PEMFC

Effect of Nitrogen-Containing Functionalization on the Electrocatalytic Activity of Ptru Nanoparticles Supported on Carbon Nanotubes for Direct Methanol Fuel Cells

Stable Pt-Ru/C catalysts prepared from new precursors by thermal reduction for direct methanol fuel cell

Method for preparing highly dispersed Pt catalysts on mesoporous carbon support

Promoting effect of nickel hydroxide on the electrocatalytic performance of Pt in alkaline solution.

The effect of Cr alloying with Pt/C as an electrocatalyst for low temperature PEM fuel cell

The Effect of Pd Precursor on Pd/Ce0.67Zr0.33O2 Catalysts for Automotive Emission Control

Effect of palladium precursor on the performance of nanorods CeO2-supported palladium catalyst for toluene catalytic combustion

Pt–SnO2/nitrogen-doped CNT Hybrid Catalysts for Proton-Exchange Membrane Fuel Cells (PEMFC): Effects of Crystalline and Amorphous SnO2 by Atomic Layer Deposition

Synthesis of a Pt/C Electrocatalyst from a User-Friendly Pt Precursor (Ammonium Hexachloroplatinate) through Microwave-Assisted Polyol Synthesis

Effect of precursors on Cu particle distribution in g-C3N4 nanosheets towards efficient photocatalytic degradation and H2 generation