The Influence of Three Groups of Pt-Ru/C Catalyst’s Precursors on Its Performance for Direct Methanol Fuel Cell

ZB Wang,GP Yin,PF Shi

DOI: https://doi.org/10.3866/pku.whxb20051019

2005-01-01

Abstract:This research is aimed to increase the activity of platinum-ruthenium alloy (Pt-Ru/C) catalysts and thus to lower the catalyst loading in anodes for methanol electrooxidation. The direct methanol fuel cell (DMFC) anode catalysts, Pt-Ru/C, were prepared from three groups of precursors by thermal reduction. The phase structure, particle size, size distribution and the morphology of reduced catalysts were determined by means of high-resolution transmission electron microscopy (TEM) and X-ray diffraction (XRD). It is found that XRD patterns of all the catalysts show Pt reflexion of a face centered cubic (fcc) crystal structure. But there are diffraction peaks indicating the presence of either pure Ru or Ru-rich hexagonal close packed (hcp) phase, which is not alloyed with Pt in PtRu/C catalysts prepared from (NH4)(2)PtCl6+Ru(OH)(3), or H2PtCl6+RuCl6 as precursors. The catalyst prepared from Pt (NH3)(2) (NO2)(2) and Ru compound of self-prepared as precursors had a more homogeneous distribution of Pt-Ru alloy in carbon and a small particle size of about 3.7 run.. Their performance was tested using a glassy carbon working electrode by cyclic voltammetry(CV), chronoamperometric and amperometric i-t curves in a solution of 0.5 mol (.) L-1 CH3OH and 0.5 mol (.) L-1 H2SO4 at 25 degrees C. The electrocatalytic activity of Pt-Ru/C catalysts prepared from Pt(NH3)(2) (NO2)(2) and Ru compound of self-prepared as precursors has the highest catalyticactivity for methanol electrooxidation. The, peak current density in CV is 11.5 mA(.)cm(-2).