Study on Structure and Electrochemical Properties of CO2 Corrosion Scales on P110 Steel Corroded at High Temperature and Pressure

LI Chun-fu,WANG Bin,DAI Jia-lin,WANG Hu,ZHANG Xian-ju,LUO Ping-ya
DOI: https://doi.org/10.3969/j.issn.1009-6264.2006.05.018
2006-01-01
Abstract:Corrosion tests of P110 steel was conducted in the extraction liquid of oil field for 4 to 144 hours by simulating the supercritical fluid condition of CO_2(35MPa,160℃)exited in deep well.The structure and electrochemical behavior of the corrosion scale were analyzed by SEM、 XRD、XPS and EIS.The results indicate that when the P110 steel contacts with the extraction liquid contained 4 mol % CO_2,the corrosion scale rapidly forms within 4 to 8 hours,and up to 48 hours,it is consisted of fine FeCO_3 crystal grains.During the period of 48 to 144 hours,the FeCO_3 scale gradually changes into a fine compound scale consisted of(Fe,Ca) CO_3,Fe_2CaCO_3 and CaCO_3 by corrosion and deposition.Due to strong bonding to the matrix,the compact structure and lack of ionic selectivity permeation passage,the thickness of scale stops increasing and is kept stable since it forms at 48 hours.It is verified by electrochemical impedance spectroscopy that the corrosion scale has good coverage on the matrix and can protect it very well.
What problem does this paper attempt to address?