Fabrication of Tin Oxide Porous Nanostructures on Titanium by Anodization and Electroplating

Weiqing Han,Gang Zhou,Lianjun Wang,Xiuyun Sun,Jiansheng Li

DOI: https://doi.org/10.3969/j.issn.1674-4926.2006.12.013

2006-01-01

Abstract:A tin dioxide nanotube is fabricated on titanium by anodization and electroplating. First, a nickel film is deposited on 3 mm-thick titanium. Then a 1 μm-thick tin layer is deposited thereon by electroplating. The wafer is anodized for 5 min in 0.5 mol/L oxalic acid solution, at constant DC 5 V at room temperature. After the anodization, to enlarge the pore size and remove the barrier layer, the anodized specimens are immersed in a 1.0 mol/L oxalic acid solution for 15 min at 80°C. The obtained samples are examined by scanning electron microscopy, EDS, and X-ray diffraction. The results indicate that a layer of nano-pore arrays of tin oxidation, whose thickness is about l μm, formed on the titanium. The pore diameter is 70 nm. The distance between two adjacent pores is 80 nm. The sample is heated to 500°C for 2 h to fabricate SnO2 compound and is used for the fabrication of composite coating on titanium also.