The Microstructure Evolution Of Type 17-4ph Stainless Steel During Long-Term Aging At 350(Circle)C

Jun Wang,Hong Zou,Cong Li,Yanhua Peng,Shaoyu Qiu,Baoluo Shen
DOI: https://doi.org/10.1016/j.nucengdes.2006.03.017
IF: 1.7
2006-01-01
Nuclear Engineering and Design
Abstract:The microstructure evolution of 17-4 precipitation hardening (17-4PH) stainless steel during long-term aging at 350 degrees C was studied mainly by X-ray diffraction and transmission electron microscopy. The results showed that the matrix is lath martensite and the precipitation of nano-metric particles of epsilon-Cu phase after the alloy has been subjected to solution and temper treatment. When the alloy is aged at 350 degrees C to 9 months, some reversed austenite is formed and the epsilon-Cu precipitates are coarsening according to ripening process. When the alloy aged from 9 to 12 months, some bulk secondary carbides, M23C6, are precipitated. With the age time extended to 15 months, an amount of reversed austenite is transformed and the G-phase, a kind of intermetallic compound, precipitation occurs nearby the epsilon-Cu precipitates in the matrix at this intermediate temperature. (c) 2006 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?