Abstract:With types of in-house-synthesized multi-walled carbon nanotubes (CNTs) and the nitrates of the corresponding metallic components, highly active CNT-promoted Cu–ZnO–Al2O3 catalysts, symbolized as CuiZnjAlk-x%CNTs, were prepared by the co-precipitation method. Their catalytic performance for methanol synthesis from H2/CO/CO2 was studied and compared with the corresponding CNT-free co-precipitated catalyst, CuiZnjAlk. It was shown experimentally that appropriate incorporation of a minor amount of the CNTs into the CuiZnjAlk could significantly increase the catalyst activity for methanol synthesis. Under the reaction conditions of 493 K, 5.0 MPa, H2/CO/CO2/N2 = 62/30/5/3 (v/v), GHSV = 8000 h-1, the observed CO conversion and methanol formation rate over a co-precipitated catalyst of Cu6Zn3Al1-12.5%CNTs reached 36.8% and 0.291 μmol CH3OH s-1 (m2-surf. Cu)-1, which was about 44 and 25% higher than those (25.5% and 0.233 μmol CH3OH s-1 (m2-surf. Cu)-1) over the corresponding CNT-free co-precipitated catalyst, Cu6Zn3Al1. Addition of a minor amount (10–15 wt%) of the CNTs to the Cu6Zn3Al1 catalyst was found to considerably increase specific surface area, especially Cu surface area of the catalyst. H2-TPD measurements revealed that the CNTs and the pre-reduced CNT-promoted catalyst systems could reversibly adsorb and store a considerably greater amount of hydrogen under atmospheric pressure at temperatures ranging from room temperature to ∼573 K. This unique feature would be beneficial for generating microenvironments with higher stationary-state concentration of active hydrogen adspecies on the surface of the functioning catalyst, especially at the interphasial active sites since the highly conductive CNTs might promote hydrogen spillover from the Cu sites to the Cu/Zn interphasial active sites, and thus be favorable for increasing the rate of the CO hydrogenation reactions. Alternatively, the operation temperature for methanol synthesis over the CNT-promoted catalysts can be 15–20 degrees lower than that over the corresponding CNT-free contrast system. This would contribute considerably to an increase in equilibrium CO conversion and CH3OH yield. The results of the present work indicated that the CNTs could serve as an excellent promoter.

Carbon nanotube-promoted cobalt-copper (or molybdenum) catalysts for higher alcohol synthesis from syngas

Synthesis of Higher Alcohols from Syngas over Alkali Promoted K-Co-Mo Catalysts Supported on Multi-Walled Carbon Nanotubes

Carbon Nanotube-Supported Copper-Cobalt Catalyst for the Production of Higher Carbon Number Alcohols Through Carbon Monoxide Hydrogenation

Hydrophobic dual metal silicate nanotubes for higher alcohol synthesis

Co–Co2C catalysts supported on carbon-coated ordered mesoporous silica with promoted CO insertion and C–C coupling for higher alcohol synthesis from syngas

Cu-Promoted Iron Catalysts Supported on Nanorod-Structured Mn-Ce Mixed Oxides for Higher Alcohol Synthesis from Syngas

Kinetic Study of Higher Alcohol Synthesis Directly from Syngas over Cocu/Sio2 Catalysts

Nanosheet-structured K–Co–MoS2 Catalyst for the Higher Alcohol Synthesis from Syngas: Synthesis and Activation

Effect of the promoter and support on cobalt-based catalysts for higher alcohols synthesis through CO hydrogenation

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst

Effects of alkali promoters on tri-metallic Co-Ni-Cu-based perovskite catalyst for higher alcohol synthesis from syngas

Targeted Design And Synthesis Of A Highly Selective Mo-Based Catalyst For The Synthesis Of Higher Alcohols

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

Highly Active CNT-Promoted Cu–ZnO–Al2O3 Catalyst for Methanol Synthesis from H2/CO/CO2

The Active Pair of Coδ+/Co0 Tailored by Nickel and CaTiO3 with Perovskite Phase for Higher Alcohols Synthesis from Syngas

Influence of Co Modified Mn/Cu/MgO Catalyst on the Synthesis of Mixed Alcohols from Syngas

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

Ternary copper–cobalt–cerium catalyst for the production of ethanol and higher alcohols through CO hydrogenation

Effect of the Dimensions of Carbon Nanotube Channels on Copper–cobalt–cerium Catalysts for Higher Alcohols Synthesis

Alkaline-Etched NiMgAl Trimetallic Oxide-Supported KMoS-Based Catalysts for Boosting Higher Alcohol Selectivity in CO Hydrogenation