Abstract:With types of in-house-synthesized multi-walled carbon nanotubes (CNTs) and the nitrates of the corresponding metallic components, highly active CNT-promoted Cu–ZnO–Al2O3 catalysts, symbolized as CuiZnjAlk-x%CNTs, were prepared by the co-precipitation method. Their catalytic performance for methanol synthesis from H2/CO/CO2 was studied and compared with the corresponding CNT-free co-precipitated catalyst, CuiZnjAlk. It was shown experimentally that appropriate incorporation of a minor amount of the CNTs into the CuiZnjAlk could significantly increase the catalyst activity for methanol synthesis. Under the reaction conditions of 493 K, 5.0 MPa, H2/CO/CO2/N2 = 62/30/5/3 (v/v), GHSV = 8000 h-1, the observed CO conversion and methanol formation rate over a co-precipitated catalyst of Cu6Zn3Al1-12.5%CNTs reached 36.8% and 0.291 μmol CH3OH s-1 (m2-surf. Cu)-1, which was about 44 and 25% higher than those (25.5% and 0.233 μmol CH3OH s-1 (m2-surf. Cu)-1) over the corresponding CNT-free co-precipitated catalyst, Cu6Zn3Al1. Addition of a minor amount (10–15 wt%) of the CNTs to the Cu6Zn3Al1 catalyst was found to considerably increase specific surface area, especially Cu surface area of the catalyst. H2-TPD measurements revealed that the CNTs and the pre-reduced CNT-promoted catalyst systems could reversibly adsorb and store a considerably greater amount of hydrogen under atmospheric pressure at temperatures ranging from room temperature to ∼573 K. This unique feature would be beneficial for generating microenvironments with higher stationary-state concentration of active hydrogen adspecies on the surface of the functioning catalyst, especially at the interphasial active sites since the highly conductive CNTs might promote hydrogen spillover from the Cu sites to the Cu/Zn interphasial active sites, and thus be favorable for increasing the rate of the CO hydrogenation reactions. Alternatively, the operation temperature for methanol synthesis over the CNT-promoted catalysts can be 15–20 degrees lower than that over the corresponding CNT-free contrast system. This would contribute considerably to an increase in equilibrium CO conversion and CH3OH yield. The results of the present work indicated that the CNTs could serve as an excellent promoter.

Carbon Nanotube-Supported Copper-Cobalt Catalyst for the Production of Higher Carbon Number Alcohols Through Carbon Monoxide Hydrogenation

Ternary copper–cobalt–cerium catalyst for the production of ethanol and higher alcohols through CO hydrogenation

Effect of the Dimensions of Carbon Nanotube Channels on Copper–cobalt–cerium Catalysts for Higher Alcohols Synthesis

Synthesis of Higher Alcohols from Syngas over Alkali Promoted K-Co-Mo Catalysts Supported on Multi-Walled Carbon Nanotubes

Ternary Cobalt–Copper–Niobium Catalysts for the Selective CO Hydrogenation to Higher Alcohols

Effect of the promoter and support on cobalt-based catalysts for higher alcohols synthesis through CO hydrogenation

Hydrophobic dual metal silicate nanotubes for higher alcohol synthesis

Highly Active CNT-Promoted Cu–ZnO–Al2O3 Catalyst for Methanol Synthesis from H2/CO/CO2

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

Effect of Hydroxyl Groups on CuCoMg Nanosheets for Ethanol and Higher Alcohol Synthesis from Syngas

Study on the Synergistic Catalysis of CeO2 Regulated Co0–Coδ+ Dual Sites for Direct Synthesis of Higher Alcohols from Syngas

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

Higher Alcohols through CO Hydrogenation over CoCu Catalysts: Influence of Precursor Activation

Syngas conversion to higher alcohols via wood-framed Cu/Co-carbon catalyst

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

Ethanol and Higher Alcohols Synthesis from Syngas over CuCoM (m=fe, Cr, Ga and Al) Nanoplates Derived from Hydrotalcite‐Like Precursors

Effects of Manganese on the Catalytic Performance of CuCo Catalysts for Direct Conversion of CO/CO2 to Higher Alcohol

CuZnAl@S-1 Catalyst for the Synthesis of Higher Alcohols by CO Hydrogenation