Abstract:Without the use of a metal catalyst in the process, ZnO with nanostructures was successfully prepared on Si (100) substrate by simple chemical vapor-deposition method. In our work, Ar was used as the plasma forming gas, O2 was the reactive gas and metal zinc powder (99.99% purity) vaporized by cylinder hollow-cathode discharge (HCD) acted as the zinc source. The crystal structures of the as-synthesized ZnO nanostructures were characterized by X-ray diffraction (XRD); the ZnO sample growing on the wall of the crucible showed a ‘comb-like’ nanostructure, while the other one at the bottom of the crucible showed a ‘rod-like’ structure, which can be attributed to the difference of the oxygen content. The measurement on the photoluminescence (PL) performance of the ZnO nanostructures was carried out at room temperature. The results indicated that the ‘comb-shape’ ZnO nanomaterial possessed a remarkably strong ultraviolet emission peak centered at 388 nm, while ZnO nanorods, except better ultraviolet emission, also had relatively strong blue-green emission ranging from 470 to 600 nm due to the existence of oxygen vacancies. The growth mechanism of ZnO with nanostructures is also discussed in this paper.

Hexagonal And Prismatic Nanowalled Zno Microboxes

Microwave-Assisted Rapid Synthesis Of Zno Hexagonal Quasi-Hourglasses

An “edge to Edge” Jigsaw-Puzzle Two-Dimensional Vapor-Phase Transport Growth of High-Quality Large-Area Wurtzite-Type ZnO (0001) Nanohexagons

Template-Free Fabrication of Hexagonal Zno Microprism with an Interior Space

ZnO Nanowire and $\hbox{ws}_{2}$ Nanotube Electronics

Hollow Microspherical Architectures of Closely Packed and Radially Well-Aligned Zn2SiO4 Nanowires with and without ZnO Nanocrust

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

4 Nm ZnO Nanocrystals Fabrication Through Electron Beam Irradiation on the Surface of a ZnO Nanoneedle Formed by Thermal Annealing

Photoluminescent Hierarchical Zno Micro‐flower and Its Surface Wettability

Highly Uv Luminescent Zno Microtetrapod-On-Nanowire Hybrids

The Synthesis and Crystallography of Some Novel ZnO Nano- and Micro-Crystals and Structures

Fabrication and characterization of hexagonally patterned quasi-1D ZnO nanowire arrays

Six-Fold-Symmetrical Hierarchical Zno Nanostructure Arrays: Synthesis, Characterization, and Field Emission Properties

Benzenedicarboxylic Acid-Assisted Synthesis of ZnO Micro-Hexagons from Zinc Hydroxide Nanostrands and Their Photoluminescence Properties

Formation Mechanism of Hollow Microspheres Consisting of ZnO Nanosheets

Microspheric Organization of Multilayered ZnO Nanosheets with Hierarchically Porous Structures

Mesoporous Single-crystal CoSn(OH)6 Hollow Structures with Multilevel Interiors

Large Scale Fabrication Of Periodical Bowl-Like Micropatterns Of Single Crystal Zno

Growth Of Zno Crystals With Branched Spindles And Prismatic Whiskers From Zn-3(Oh)(2)V2o7 Center Dot H2o Nanosheets By A Hydrothermal Route

Three-dimensional Six-Fold Symmetry ZnO Sub-Microstructures

Controllable Synthesis of Hexagonal, Bullet-Like Zno Microstructures and Nanorod Arrays and Their Photocatalytic Property