Abstract:To improve the wear resistance of TC4 titanium alloy, two types of wear-resistant coatings were applied to the surface using laser melting: Ni60 + 50% WC and d22 powder priming. The phase composition and microstructure of the coatings were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), and energy spectroscopy (EDS). The mechanical properties of the coating were tested using an HV-1000 micro-Vickers hardness tester, an HRS-2M high-speed reciprocating friction and wear tester, and a WDW-100D electronic universal testing machine. The results show that Ni60 + 50% WC composite coating and d22 priming + (Ni60 + 50% WC) composite coating mainly consist of W2C, TiC, Ni17W3, Ni3Ti, and TixW1−x phases. Compared to the TC4 substrate, the microhardness of both coatings is significantly higher, approximately 2.8 times the microhardness of the substrate. In frictional wear experiments, the average friction factors of the two coatings and the TC4 substrate are 0.476, 0.55, and 0.865, respectively, and the wear of the two coatings is only 0.0559–0.0769 that of the TC4 substrate, with a significant increase in wear resistance, nearly 17 times higher than that of the substrate. The coating shows flaking, shallow abrasion marks, and granular debris, dominated by adhesive wear and fatigue wear, while the TC4 substrate shows more furrows on the surface, dominated by abrasive wear. The shear bond strengths of the Ni60 + 50% WC composite coating and the d22 powder primed + (Ni60 + 50% WC) composite coating were 188.19 MPa and 49.11 MPa, respectively. Conclusion: both coatings significantly improve the hardness and wear resistance of the TC4 titanium alloy substrate surface, with the Ni60 + 50% WC composite coating performing better in hardness, wear resistance, and bond strength.

Wear properties of alloyed layers produced by laser surface alloying of pure titanium with B 4 C and T{i} mixed powders

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

Laser Surface Alloying of Pure Titanium with TiN–B–Si–Ni Mixed Powders

Analysis of the growth mechanism of TiC crystal and the mechanical properties of the laser alloyed layer on the surface of pure titanium

Microstructures And Wear Properties Of The Composite Coatings Laser-Fabricated On Titanium Alloy Ti-6al-4v

Microstructure Evaluation and High-Temperature Wear Performance of Hard Protective Layer Deposited on Titanium Alloy via Laser Metal Deposition

Microstructure and Mechanical Properties of a Ti-6Al-4V Titanium Alloy Subjected to Laser Cladding

MICROSTRUCTURE AND WEAR PROPERTY OF Ti/C MODIFIED LAYERS ON Ti-6Al-4V SUBSTRATE

Surface Modification of Pure Ti by Laser Alloying with B and Ni Mixed Powders

Microstructure and wear resistance of laser clad composite coating on TC4 titanium alloy surface

Study of Laser Cladding Three Pre-Placed Powders on Titanium Alloy

Microstructure, wear resistance and cell proliferation ability of in situ synthesized Ti–B coating produced by laser alloying

Microstructure, wear and corrosion properties of B-C composite layers on pure titanium

Wear and corrosion properties of a B–Al composite layer on pure titanium

Microstructure and anti-ablation of laser cladding Ti-Zr-B-C coating on TC11 titanium alloy

Wear and Oxidation Resistance Coatings Fabricated on Ti-6al-4v by Laser Surface Alloying Technique

Microstructure and Wear Resistance of Laser Cladding TiC Coat on Titanium Alloy

Microstructure and Tribological Properties of NiCrBSi-TiC Laser Clad Layer on Titanium Alloy Substrate

Study of the Performance of Laser Melting Wear-Resistant Coatings on TC4 Titanium Alloy Surfaces

The Wear Behavior of the Laser Cladded Ti-Al-Si Composite Coatings on Ti-6Al-4V Alloy with Additional TiC

Laser Synthesis of Titanium Aluminides Matrix Composite Coatings Reinforced by In-Situ Titanium Carbide Particles on Ti-6Al-4V Substrate