Abstract:An economical gradient layer was successfully prepared on Ti6Al4V alloy produced by laser powder bed fusion (L-PBF) using only composition design, gravity segregation, and laser cladding of micrometer-sized Ni powder, nanoscale SiC and Y 2 O 3 powders. The microstructure of the layer was systematically studied to analyze the reasons for its improved wear and corrosion resistance. The results indicated that the cladding layer comprised top, middle, lower, and bottom layers. The main phases in top layer were Ti 2 Ni and β-Ti. Whereas the middle layer is composed of two regions, one with a similar structure to the top layer, and the other is the nickel-enriched area denoted as NEAm where the main phases were Ti 2 Ni, TiNi, and amorphous. The main phase of the lower layer was TiNi. Owing to the close distance between the bottom layer and the substrate, there was a significant increase of Ti in the bottom layer, and so the bottom layer and the top layer contained the same main phases. The soft phase of TiNi in lower layer would prevent the propagation of cracks that may occur in the top layer. The solidification and formation process of the gradient structure of the cladding layer was analyzed with Scheil model, and the simulation results were consistent with the experimental results. A nanocomposite system consisting of Ti 3 Si, α-Ti, and β-Ti was found for the first time in this study. The relationship between Ti 3 Si and α-Ti was coherent, and the relationship between α-Ti and β-Ti satisfied the Burgers orientation relationship. The mechanism of the nanocomposite system generation was that Si was enriched at the grain boundaries after the formation of Ti 2 Ni, where Ti and Si combined to form Ti 3 Si, and then Ti 3 Si was used as nucleating particles to form β-Ti/α-Ti. The α-Ti and β-Ti in the fusion line area at the bottom layer also satisfied the Burgers coherent relationship, indicating excellent bonding strength between cladding layer and substrate. A large number of solute atoms in the solid solution, pinning of second-phase particles, and the amorphous were the fundamental reasons for the substantial improvement in hardness and wear resistance. A small amount of Ni in the top layer increased the polarization of the cathodic reaction, keeping the corrosion current low. In addition, numerous dispersed fine phases in the top layer increased the resistance of charge transfer at the phase interfaces, which was the fundamental reason for the improved corrosion resistance.

Laser Surface Alloying of Pure Titanium with TiN–B–Si–Ni Mixed Powders

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Microstructure and Hardness of the Laser Surface Treated Titanium

Process optimization and property of Ti-Al-Cr-Nb coating on titanium alloy surface by laser in-situ synthesis

Microstructural and Performance Analysis of (TiAl)95−xCu5Nix Coatings Prepared via Laser Surface Cladding on Ti–6Al–4V Substrates

Surface nitridation of titanium using pulse laser gas alloying method and its microstructure analysis with XRD and SEM

In-situ TiB2-TiC reinforced Fe-Al composite coating on 6061 aluminum alloy by laser surface modification

Laser Synthesis of Titanium Aluminides Matrix Composite Coatings Reinforced by In-Situ Titanium Carbide Particles on Ti-6Al-4V Substrate

Microstructure and Properties of Ti6Al4V Surface Processed by Continuous Wave Laser in Different Atmospheres

Microstructure and performance optimization of laser cladding nano-TiC modified nickel-based alloy coatings

Microstructure and tribological properties of laser in-situ synthesized Ti3Al composite coating on Ti-6Al-4V

Influence of Scanning Speed on the Microstructure and Wear Resistance of Laser Alloying Coatings on Ti-6Al-4V Substrate

Effect of TiO2 on the Laser Cladding Layers of Ni-based Alloy on 45# Steel

Microstructure Evaluation and High-Temperature Wear Performance of Hard Protective Layer Deposited on Titanium Alloy via Laser Metal Deposition

Microstructure, wear resistance and cell proliferation ability of in situ synthesized Ti–B coating produced by laser alloying

On the novel precipitation sequence of the TiN modified Al-Mn-Sc alloy processed by laser powder bed fusion

Microstructure and Properties of Ni-Ti Based Gradient Laser Cladding Layer of Ti6Al4V Alloy by Laser Powder Bed Fusion

Microstructure regulation and performance of titanium alloy coating with Ni interlayer on the surface of mild steel by laser cladding

Improving the Bio-Tribological Properties of Ti6Al4V Alloy via Combined Treatment of Femtosecond Laser Nitriding and Texturing

Microstructure and Wear Resistance of Ti6Al4V Titanium Alloy Laser-Clad Ni60/WC Composite Coating

The Interplay of Thermal Gradient and Laser Process Parameters on the Mechanical Properties, Geometrical and Microstructural Characteristics of Laser-Cladded Titanium (Ti6Al4V) Alloy Composite Coatings