Influence of Silver Coating on the Structure and Properties of LiFePO4

Junbiao Lu,Bin Le,Zilong Tang,Zhongtai Zhang,Junrong Li,Wanci Shen

DOI: https://doi.org/10.3321/j.issn:1002-185X.2005.z2.016

2005-01-01

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

Abstract:with the dispersant of PEG AgNO3 and pretreated LiFePO 4 were mixed by ball mill. And then Oliver phased LiFePO4 coated by silver was synthesized. Comparing with blank sample, LiFePO 4 coated by silver shows fine particle and almost same size. The BES and element distribution photograph reveal the well distribution of silver in the samples. The XPS spectrum of LiFePO4 surface reveals the existence and the valence of silver. Cyclic voltammetry curve show the only mechanism for lithium ion extraction/ insertion in cathode material. Along with the increasing of current density, the capacity shows no obviously change, but electrode polarity effect was gradually increased. When cycled at current density of C, battery show large electrode polarity effect and low capacity. When decrease current density to C/10, battery delivers capacity of original values again. At the current density of C/8, battery was cycled 45 times, no obviously cycle fade can be observed.