Abstract:Phase morphology, mechanical properties, melt rheology, and failure mechanisms of polypropylene (PP) blended with 0–30% (by weight) of ethylene- n -butyl acrylate-carbon monoxide (E- n BA-CO) were studied. A typical matrix/dispersed-droplet morphology was observed for all blends together with a relatively coarse dispersion of modifier domains in the blends having more than 20% (by weight) of E- n BA-CO. Binary blends showed tremendous improvements in tensile ductility compared with neat PP. The elastic modulus, yield stress, and tensile strength decreased steadily with E- n BA-CO loading in the blend, but the degree of reductions was insignificant and the blends exhibited a good balance of tensile properties. The impact strength on notched samples increased sharply with E- n BA-CO content up to 10% (by weight) and then decreased at higher modifier contents. E- n BA-CO did not influence the crystallization and melting characteristics of PP matrix. E- n BA-CO changed the rheological behavior of PP, and melt viscosity and elasticity for the blends increased in direct proportion to the E- n BA-CO fraction. A transition from a liquid-like response to a nearly solid-like one at low-frequency regions was detected with the progressive incorporation of E- n BA-CO into the PP matrix. Fractography analysis of impact-fractured samples revealed some localized, small-scale plastic deformations along with a relatively poor interfacial adhesion across the phase boundaries between the dispersed domains and the surrounding PP matrix. Extensive interfacial debonding–cavitation and pull out of dispersed domains were responsible for the low impact toughness for the blends containing more than 15% (by weight) of E- n BA-CO.

PREDICTION OF THE PAILURE STRENGTH OF POLYPROPYLENE/POLYAMIDE 1010 BLEND

Poly(L-Lactide) Materials with Balanced Mechanical Properties Prepared by Blending with Peg-Mb-Ppa Multiblock Copolymers

MECHANICAL PROPERTIES AND MORPHOLOGY OF POLYPROPYLENE/POLYSTYRENE BLENDS*

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Relationship between structure and properties in high-performance PA6/SEBS-g-MA/(PPO/PS) blends: The role of PPO and PS

Comparison Among Three Different Approaches to Dynamic Damage Measurement for Polymer Blends

On the phase inversion of polypropylene/polystyrene blends

Microstructures and Mechanical Properties of Polypropylene/polyamide 6/Polyethelene-Octene Elastomer Blends

Study on Toughening Mechanism of Low Molecular Weight PC/PP Blend

Preparation and Properties of Solvent Resistance PC/PA1010 Blends

Analysis of phase morphology and dynamics of immiscible PP/PA1010 blends and its partial-miscible blends during melt mixing from SEM patterns

Morphology, thermal behavior, rheological, and mechanical properties of polypropylene/polystyrene blends based on elongation flow

STUDY ON THE ELASTIC MODULUS POLYPROPYLENE/POLYSTYRENE BLENDS BY MESO-MECHANICS

Influences of component ratio of minor phases and charge sequence on the morphology and mechanical properties of PP/PS/PA6 ternary blends

Realizing Simultaneous High‐temperature Strength and Low‐temperature Elongation in Polyolefin Elastomer Toughened Polypropylene Via Controlling the Dispersed Phase Size

Study on the Microstructures and Mechanical Behaviour of Compatibilized Polypropylene/Polyamide-6 Blends

Study on Mechanical Properties of PP/UHMWPE Blends

Polypropylene toughened with ethylene-n-butyl acrylate-carbon monoxide terpolymer: structure–property relationship

Novel Method for Preparation of Polypropylene Blends with High Melt Strength by Reactive Compounding

Toughening Mechanism of Polypropylene Bends with Polymer Particles in Core-Shell Structure: Equivalent Rubber Content Effect Related to Core-Shell Interfacial Strength

Fabrication and toughening mechanism of high toughness PP/SEBS/HDPE blends with core‐shell particles