Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Room Temperature Self-Assembly Growth of Cobalt Nanowires under Magnetic Fields

Magnetic field-induced growth and self-assembly of cobalt nanocrystallites

Synthesis of Cobalt Nanowires by Template-Free Method

Synthesis of Cobalt Nanowires in Aqueous Solution under an External Magnetic Field

Synthesis and One-Dimensional Self-Assembly of Acicular Nickel Nanocrystallites under Magnetic Fields

Growth of Dendritic Cobalt Nanocrystals at Room Temperature

Assembly of non-crystalline cobalt particles into crystalline tricobalt tetroxide nanowires under an external magnetic field

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

A Hydrothermal Reduction Route to Single‐Crystalline Hexagonal Cobalt Nanowires

On the Growth Mechanism of Nickel and Cobalt Nanowires and Comparison of Their Magnetic Properties

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Individually grown cobalt nanowires as magnetic force microscopy probes

The influence of magnetic field on the crystal growth of electrodeposited Co nanowires

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Superstructures of Self-Assembled Cobalt Nanocrystals

Hydrothermal Microemulsion Synthesis of Cobalt Nanorods and Self-Assembly into Square-Shaped Nanostructures

Growth of single-crystalline Co 7 Fe 3 nanowires via electrochemical deposition and their magnetic properties

Effect of Size Distribution on Magnetic Properties in Cobalt Nanowires

Controlled Synthesis of Co3o4 Nanocubes under External Magnetic Fields and Their Magnetic Properties

Preparation of cobalt nanocrystals in the homogenous solution with the presence of a static magnetic field