Preparation and characterization of fibrous Ni-Co alloy powders by thermal decomposition of solid solution of complex Ni-Co oxalates

Chuanfu Zhang,Jing Zhan,Jianhui Wu

2005-01-01

Abstract:Synthesis of fibrous Ni-Co alloy powders was achieved by thermal decomposition of precursor of complex Ni-Co oxalates solid solutions obtained via modified coprecipitation method among intimate mixing solution of NiCl 2·6H2O, CoCl2·6H2O and H2C2O4·2H2O in the presence of surfactant polyvinylpyrrolidone (PVP) and organic solvent ethanol. Scan electron microscopy (SEM), X-ray diffraction (XRD), X-Ray photoelectron spectroscopy (XPS), disperse energy X-ray analyses (EDX) were used to characterize the structure features and chemical compositions of the as-prepared fibres. The influences of decomposition conditions, including temperature, time, the flow rate of N2+H2, and the heating rate, on the morphology, average size and specific surface area of the Ni-Co alloy powders were investigated. It is found that a trend of the mutual alloying of nickel and cobalt: the formation of perfect solid solution for any compositions Ni xCo100-x was indicated and corresponding Ni xCo100-x alloys with fcc phase can be obtained under the optimal conditions.