Abstract:Taking the nucleation and compositional undercooling criterion and assuming, that the maximum interface growth temperature of phase growth is more stability during the directional solidification, microstructure selection maps for peritectic alloys from initial transient to steady state are developed, which takes into account the conditions when stable composition gradient has not been reached at the plane front directionally solidified at low growth rates and the history-dependant growth of a phase. These maps can explain the experimental phenomena appropriately due to consider the transitions of phase and microstructure during the whole process of solidification.

Formation Mechanism of Band Structure and Phase Selection During Directional Solidification of Peritectic Alloys - Ii. Phase Selection