Abstract:Using Fe as catalyser, Si nanowires (SiNWs) with diameters of 5–15nm and lengths of ∼μm were synthesized via vapor–liquid–solid growth method at high temperature. The as-prepared SiNWs with the Raman peak positions of ⩽511cm−1 show a strong photoluminescence (PL) peak centered at 745nm. The position of the PL peak exhibits no dependence on the SiNW diameters, but its intensity increases with decreasing the SiNW diameters. When the as-prepared SiNWs were gradually oxidized, the 745nm PL peak reduces its intensity and meantime a new PL peak appears at 620nm. When the SiNWs were completely oxidized, the 745nm PL vanishes and the 620nm PL peak reaches its maximal intensity. Spectral analyses and microstructural observations suggest that the 745nm PL arises from optical transition in the interfacial defect states between the SiNW core and the surface Si oxide, whereas the photogeneration of carriers takes place in the quantum confined SiNW core. Based on the electron paramagnetic resonance result, we correlate the 620nm PL with the nonbridging oxygen hole centers at the surfaces of the SiNWs.

Self-assembled Growth and Blue Emission of a SiOx-capped (x = 0.5–0.8) Silicon Nanowire Array

Self-Assembled Growth and Enhanced Blue Emission of Sioxny-Capped Silicon Nanowire Arrays

Self-Assembled Growth and Optical Emission of Silver-Capped Silicon Nanowires

Intense Violet and Blue Light Emission from Si Nanowires Fabricated Via Solid–liquid–solid Growth from Amorphous Si Films

Fabrication and Short-Wavelength Light Emission of Si Nanowires Grown Via Quasi Solid–liquid–solid Mechanism

Self-organized Growth and Optical Emission of Silicon-Based Nanoscale Β-Sic Quantum Dots

Enhanced Blue-Orange-Red Light Emission From Nc-Si:H/Sio2 Pillar Arrays Using Nanosphere Lithography

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Optical Emission from C60-molecule-coupled Si Nanocrystallites

A Novel Sulfide-Assisted Growth of Silicon Nano-Wires

Blue-light Emission from Amorphous SiOx Nanoropes

Synthesis and Photoluminescence Properties of Amorphous Siox Nanowires

Si-based Nanoscale SiO2 Islands and Light-Emitting Source Array

A Simple Route to Growth of Silicon Nanowires

Amorphous SiOx Nanowires Catalyzed by Metallic Ge for Optoelectronic Applications

Iron-Assisted Vapor-Phase Hydrothermal Method: A Low-Temperature Approach To Synthesize Blue Light Emissive SiOx Nanowires with Single-Crystal Structure of P21212

Long-persistent luminescence in near-ultraviolet from silicon nanowires

Cu Oxide Nanowire Array Grown on Si-based SiO2 Nanoscale Islands Via Nanochannels

Large-scale synthesis and photoluminescence properties of SiC/SiOx nanocables

Origin of strong white electroluminescence from dense Si nanodots embedded in silicon nitride.

Light emission from as-prepared and oxidized Si nanowires with diameters of 5–15 nm