Abstract:In this paper, high-quality nanosized Ce 0.8 Sm 0.2− x Zn x O 2− δ ( x = 0, 0.02, 0.04, 0.08, and 0.16) powders are successfully synthesized by sol–gel process for intermediate-temperature solid oxide fuel cell (IT-SOFC) application. The thermal behavior, porosity, crystal phase, surface microstructure, and electrical properties of Ce 0.8 Sm 0.2− x Zn x O 2− δ are studied by thermogravimetric-differential scanning calorimeter (TG-DSC), Archimedes drainage method, X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical impedance spectroscopy (EIS), respectively. The results show that Ce 0.8 Sm 0.2− x Zn x O 2− δ electrolyte appears very high sintering activity even at sintering temperature as low as 1300 °C. The crystal phase of sample powders after sintered at 600 °C belongs to single-phase cubic fluorite structure with mean particle size of 15 nm. The lattice parameter increases first until doping 2 mol.% Zn and then decreases with more doping amount. Electrochemical performance results demonstrate that doping with appropriate amount of Zn can significantly improve the conductivity of SDC materials. The highest conductivity of 0.057 S·cm −1 at 800 °C is obtained for Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ , owing to high density, ultrafine grains, and increased grain boundaries. Furthermore, the fuel cell performance of Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ electrolyte is measured with 5 wt.% Fe-loaded activated carbon as the fuel. It delivers an outstanding performance, with an OCV of 1.02 V, a maximum power output of 408 mW·cm −2 at 850 °C, indicating that Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ may have potential application for IT-SOFC electrolyte materials.

Direct Preparation Of Ce0.8sm0.2o1.9 Powders Oxidized With H2o2 For Low Temperature Sofcs Application

Low-temperature Solid Oxide Fuel Cells with Novel La0.6Sr0.4Co0.8Cu0.2O3−δ Perovskite Cathode and Functional Graded Anode

A cathode-supported SOFC with thin Ce0.8Sm0.2O1.9 electrolyte prepared by a suspension spray

Polyvinyl alcohol-induced low temperature synthesis of CeO2-based powders

Preparation and characterization of nanocrystalline Ce0.8Sm0.2O1.9 for low temperature solid oxide fuel cells based on composite electrolyte

Electrochemical Performance of a Solid Oxide Fuel Cell Based on Ce0.8Sm0.2O2−δ Electrolyte Synthesized by a Polymer Assisted Combustion Method

Characteristics of Li2CO3 as sintering aid for Ce0.8Sm0.2O2−δ electrolyte in solid oxide fuel cells

Direct synthesis of Ce0.8Sm0.2−xZnxO2−δ electrolyte by sol–gel for IT-SOFC

High Performance Low-Temperature Solid Oxide Fuel Cells Based on Nanostructured Ceria-Based Electrolyte

High-performing and stable non-doped ceria electrolyte with amorphous carbonate coating layer for low-temperature solid oxide fuel cells

Facile synthesis of ceria-based composite oxide materials by combustion for high-performance solid oxide fuel cells

Low Temperature Solid Oxide Fuel Cells with Hierarchically Porous Cathode Nano-Network

Development of Novel Low-Temperature SOFCs with Co-Ionic Conducting SDC-carbonate Composite Electrolytes

Fabrication, Sintering and Electrical Properties of Cobalt Oxide Doped Gd0.1Ce0.9O2−δ

Boosting Electrochemical Performance of Ho3+and Sm3+co-doped CeO2 Intermediate-Temperature Solid Oxide Membrane Fuel Cells by NiO

Preparation and Performance of Nanostructured Porous Thin Cathode for Low-Temperature Solid Oxide Fuel Cells by Spin-Coating Method

Sintering of Ce0.8Sm0.2O1.9

Conductivity Of Yttria-Doped Ceria Electrolyte Made By Chemical Coprecipitation And Its Evaluation For Sofc Application

Sintering of Ce（0.8）Sm（0.2）O（1.9）

Low Temperature Co-Sintering of Sr2Fe1.5Mo0.5O6−δ–Gd0.1Ce0.9O2−δ Anode-Supported Solid Oxide Fuel Cells with Li2O–Gd0.1Ce0.9O2−δ Electrolyte

Synthesis and Properties of SDC Powders and Ceramics for Low Temperature SOFC by Stearic Acid Process