Surface Modification in Manufacture of Β-Tricalcium Phosphate/poly(l-Lactic Acid) Composite Scaffold Materials

LI Yong,ZHANG Yun,YIN Guang-fu,ZHOU Da-li,WANG Yue-hua
DOI: https://doi.org/10.3321/j.issn:1001-9731.2005.02.043
2005-01-01
Abstract:Several surface modifying agents (polycrylic acid,trimethyl silicane,monophosphate,and palmlitic acid) were used in surface modification of β-tricalcium phosphate(β-TCP )power, and the palmitic acid was selected as the optimized surface modifying agents. Then the modification parameter was determined, and the modification effect had been tested. SEM observations indicated that the surface modified β-TCP microparticles dispersed uniformly and the diameter of microparticles were about 0.2~1.0μm. The contact angle of modified β-TCP powder for distilled water reached 145.5°, The results showed that β-TCP microparticles modified with 1wt% palmitic acid under 20min ultrasonic dispersion possessed a good hydrophobic property, and could be uniformly distributed within PLLA matrix. The mechanical properties of β-TCP/PLLA could be improved by treating the surface of β-TCP reinforcing particles with palmitic acid. The bending strength and the compressive yield strength of the composite materials had been respectively increased 63.4 %and 12.8%. The interfacial intension could be reinforced in composite materials with the modified β-TCP.
What problem does this paper attempt to address?