Penetration Performance and Fragmentation Mechanism Behind Target of Tungsten Fibre/zirconium-Based Bulk Metallic Glass Matrix Composite Rod
Feng Zhou,Chengxin Du,Chun Cheng,Lizhi Xu,Zhonghua Du,Guangfa Gao,Anbo Liu,Huameng Fu
DOI: https://doi.org/10.1016/j.ijrmhm.2023.106160
IF: 4.804
2023-01-01
International Journal of Refractory Metals and Hard Materials
Abstract:A tungsten fibre/zirconium-based bulk metallic glass matrix composite (WF/Zr-MG) is a type of armour piercing material with significant development potential. When it penetrates a finite-thickness target plate, it results in damage different from those generated by W alloys. Therefore, the penetration of 80% WF/Zr-MG by volume fraction (the diameter of the W fibre is 0.3 mm) into a 120-mm-thick 45 steel target plate is investigated experimentally at an impact velocity of 1600 +/- 20 m/s. Subsequently, the results are comp rod ared with those of a 91 Walloy (91 W) rod to investigate the penetration performance and damage ability behind the target of composite materials. The damage effects of the 45 steel target plate and after-effect target are analysed. The penetration performance and fragmentation mechanism of the two materials are analysed experimentally and based on theoretical calculations. The experimental results indicate that the WF/Zr-MG rod shows self -sharpening in the nose, a smaller average crater diameter, less kinetic energy loss, and better penetration per-formance compared with the 91 W rod. The bonding force between the phases of WF/Zr-MG is significantly lower than that of 91 W, and cracks formed easily in the material during the penetration process. Radial stress is released instantaneously after the WF/Zr-MG rod departs from the target; consequently, the WF/Zr-MG rod underwent radial expansion, fracture, and dispersion. The damaged areas of WF/Zr-MG measured 1734 and 1661 cm2, which exhibit fragment diffusion angles of 46.5 degrees and 46.1 degrees, respectively. However, the damaged areas of the W alloy are only 1017 and 1193 cm2, and the corresponding fragment diffusion angles are only 35.3 degrees and 37.8 degrees, respectively. The damage parameters of WF/Zr-MG behind the target are greater than those of the tungsten alloy, which increased its killing capacity behind the target.