Temperature and Pressure Behavior of the Emission Bands from Mn-, Cu-, and Eu-doped ZnS Nanocrystals
FH Su,ZL Fang,BS Ma,K Ding,GH Li,SJ Xu
DOI: https://doi.org/10.1063/1.1650894
IF: 2.877
2004-01-01
Journal of Applied Physics
Abstract:The temperature and pressure dependence of the photoluminescence from ZnS:Mn2+, ZnS:Cu2+, and ZnS:Eu2+ nanocrystals were investigated in the temperature range from 10 to 300 K and under hydrostatic pressure up to 6 GPa at room temperature. The orange emission (590 nm) from the T14-6A1 transition of Mn2+ ions, the green emission (518 nm) from the 4f65d1-4f7 transition of Eu2+ ions and the blue emission (460 nm) related to the transition from the conduction band of ZnS to the t2 level of Cu2+ ions were observed in the Mn-, Eu-, and Cu-doped samples, respectively. It was found that all of these emission bands decrease in intensity with increasing temperature. Among them the intensity of the Mn-orange emission dropped faster. The activation energies were estimated to be 58, 16, and 42 meV for the Mn-orange, Eu-green, and Cu-blue emissions, respectively. A negative pressure coefficient of −26 meV/GPa was obtained for the Mn-orange emission, which agrees with the value calculated from the crystal field theory. The pressure coefficient of the Cu-blue emission was found to be 62 meV/GPa, which is almost same as the value of the band gap of bulk ZnS. However, the pressure coefficient of the Eu-green emission is 23 meV/GPa, which is contrary to the predication by the crystal field theory. The strong interaction between the 4f65d1 state of the Eu2+ ions and the conduction band of ZnS may be the origin for the positive pressure coefficient and the small thermal activation energy of Eu-green emission.