Abstract:Ba 0.5 Sr 0.5 Al x Fe 12-x O 19 was synthesized by systematically altering the Al-to-Fe content ( x = 0, 1, 2, 3, 4) through the substitution of iron cations with an equivalent amount of aluminum cations. The powder was synthesized using the sol – gel auto-combustion method, resulting in a well-defined particle size distribution. This work aims to study the synthesis conditions for preparing barium strontium hexaferrite, and then the material properties was characterized by Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC), X-ray Powder Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR), and Vibrating Sample Magnetometer (VSM). The structure of the Al-substituted hexaferrite sample was confirmed using X-ray diffraction with the presence of a hexagonal phase. Using FESEM, the average particle size was found to be 76.35 nm. The magnetic properties of the barium strontium hexaferrite (BSFO) and the Al-substituted BSFO material were studied at room temperature using VSM by knowing the value of coercivity (H c ), saturation magnetization (M s ), retentivity (M r ), squareness ratio (M r /M s ) for the permanent magnet application. The M-H loop and B-H loop provide insights into the ferromagnetic characteristics of the material. Additionally, the material is assessed to determine its maximum energy storage capacity, denoted as (BH) max . The coercivity of the material was increased from 5206 to 9189 Oe whereas, the saturation value decreased with the increase in the content of Al. The energy product (BH) max for pure BSFO was 13 kJ/m 3 and this value were also estimated for different compositions of the material.

Effect of precursor solutions with different composition on synthesis of ultrafine BaLa0.3Fe11.7O19 using SHS of sol-gel

Effect of Precursor Solutions with Different Composition on Synthesis of Ultrafine BaLa0.3Fe11.7O19using Sol-Gel Auto-Combustion Technique

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Structural Analysis for Preparing Substituted Sr Hexaferrite Nanoparticles by Sol-gel Method

Key Step in Synthesis of Ultrafine BaFe12O19 by Sol-Gel Technique

Magnetic properties of nanocrystalline BaFe12 O19 prepared by ultrasonic-solid phase synthesis

A Better Preparation Process on Formation of BaFe12O19 Nanoparticles

Influence of Roasting on the Phase Composition and Magnetic Properties of BaFe12O19 Nanoparticles Prepared by Sol-Gel Self-propagation High-temperature Synthesis

Preparation and Magnetic Properties of Barium Hexaferrite Nanoparticles Produced by the Citrate Process

Synthesis of Barium Ferrite Ultrafine Powders by a Sol–gel Combustion Method Using Glycine Gels

Synthesis, characterization and magnetic properties on nanocrystalline BaFe12O19 ferrite

Synthesis and Characterization of Nd Doped M-type Hexagonal Barium Ferrite Ultrafine Powders

Molten salt synthesis and magnetic properties of BaFe12O19 hexaferrite

Synthesis of Hexagonal Barium Ferrite Nanoparticle by Sol-Gel Method

Effect of poly sodium-p-styrenesulfonate on the phase formation and morphology of the hydrothermally synthesized bismuth ferrite powders

Preparation of BaFex(Ti0.5Mn0.5)12-xO19(X=8,9,10,11,12) by Sol-Gel Self-Propagating Method

Effect of Al substitution on their structural and magnetic properties of Ba0.5Sr0.5Fe12O19 prepared via sol–gel auto-combustion method

Solvent-free synthesis of hexagonal barium ferrite (BaFe 12 O 19 ) particles

Preparation of M-Ba-ferrite Fine Powders by Sugar-Nitrates Process

Phase controlled synthesis of (Mg, Ca, Ba)-ferrite magnetic nanoparticles with high uniformity

Nano-sized powders of SrFe_(12)O_(19) synthesized by the sol-gel method