Study on Ba2+ Doping SrBi4Ti4O15 Ferroelectric Ceramics and their Dielectric Behaviors
Xie Dan,Pan Wei,Ren Tianling,Zhang Zhigang,Liu Litian,Dang Zhimin
DOI: https://doi.org/10.3321/j.issn:1002-185X.2005.z2.121
2005-01-01
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
Abstract:Bi-layered structural ferroelectric powders Sr1-xBa xTi4O15(SBBT) (x=0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) were prepared using Sol-Gel method. SBBT ceramics were obtained by sintering SBBT powders at 1060°C-1120°C. The sintering temperature of SBBT ceramics with different Ba2+ doping contents is different. As the contents of Ba2+ increase, the sintering temperature decreases, 1120°C for SrBi4Ti4O15(SBTi) and 1060°C for BaBi4Ti4O15(BBTi). And the surface morphology and grain size of SBTi and BBTi ceramics are different. BBTi ceramics contain more and larger plate-like grains than that in SBTi, the size of the grains in BBTi ceramics is about 8μm-10μm and the thickness is about 2.5 μm. The doping of Ba2+ affects not only the morphology and grain size of SBBT ceramics, but also their dielectric behavior. With the increase of Ba2+ doping contents, dielectric constant increases first and then decreases, while dissipation decreases first and then increases. At the molar ratio of Sr:Ba=0.5:0.5, measuring frequency about IkHz, SBBT ceramics exhibit the highest dielectric constant(290) and lowest dissipation(0.5%).