Preparation of Porous Glass-ceramic with Controlled Pore Size and Porosity by Adding Porosifier

和峰,刘昌胜
DOI: https://doi.org/10.3321/j.issn:1000-324X.2004.06.008
IF: 1.292
2004-01-01
Journal of Inorganic Materials
Abstract:This study presents the manufacture of highly porous biological glass-ceramic with interconnected pores by adding porosifier, and its main crystallized products are fluroapatite and wollastonite. The effects of preparation conditions involving porosifier deformation during pressing (die-pressing technique), particle size and content, and forming pressure on the resultant porosity, pore size as well as structure and mechanical properties were investigated. The experimental results demonstrate that the resultant porous glass-ceramic with a successful control of pore size and 50% similar to 82% volume fraction porosity can be obtained. Macropores with 250 similar to 850mum diameter forming through the pyrolysis of porosifier interconnect through the holes with 50 similar to 300mum diameter in pore wall. Very little pore volume results from micropores with 2 similar to 4mum diameter because of the incomplete sintering of glass particles. Due to plastic deformation under pressure, the green body that is added plastic porosifier stearic acid is with high-strength and can be machined into complex shape, and the sintered products with flat-sphere shape macropores are with high-strength also. On the contrast, because of elastic deformation of rigid porosifier polystyrene under pressure, green body is with low-strength and can't be machined, and the sintered products with round-sphere shape macropores are with low-strength also. The forming pressure has a strong impact on the properties of samples with plastic porosifier stearic acid, but do not influence the properties of samples with rigid porosifier polystyrene significantly. The total porosity correlates with the weight content of porosifier linearly, so the porosity and pore diameter can be controlled through controlling the porosifier size and its content. The compressive strength increases with increased porosity and correlates with the total porosity by a quadratic with certain pore diameter, so it can be predicted through porosifier content.
What problem does this paper attempt to address?