Abstract:Poly(amic acid)s (PAAs) alignment agents have been prepared from the alicyclic dianhydrides, including 1,2,3,4‐cyclobutanetetracarboxylic dianhydride (CBDA, I), 1,3‐dimethyl‐1,2,3,4‐cyclobutanetetracarboxylic dianhydride (DMCBDA, II), and ester‐linked aromatic diamines, including 4‐aminophenyl‐4′‐aminobenzoate (APAB, a) and bis(4‐aminophenyl)terephthalate (BPTP, b), respectively. The derived PAAs, including PAA‐Ia (CBDA‐APAB), PAA‐Ib (CBDA‐BPTP), and PAA‐IIa (DMCBDA‐APAB) exhibited the preferable molecular weights, while the PAA‐IIb (DMCBDA‐BPTP) showed the low one due to the low polymerization reactivity both for the DMCBDA dianhydride and the BPTP diamine. All the PAA solutions except PAA‐IIb were adopted as the alignment components to fabricate liquid crystal (LC) minicells with a mode of in‐plane switching (IPS). The polyimides (PI) alignment layers derived from the thermal dehydration reaction of the PAA precursors at 230°C for 30 min showed good alignments effects to the LC molecules, which exhibited the pretilt angles (θp) from 0.09 to 0.15° after being exposed by the linear polarized ultraviolet light sources with the wavelength of 254 nm. In addition, the PI alignment layers afforded good optoelectronic features to the minicells, including the voltage holding ratio values over 97% at room temperature, and the residual direct circuit voltages lower than 1.0 V. The anchoring energy results indicated that the PI‐IIa (DMCBDA‐APAB) alignment layer showed the highest interaction with the LC molecules, and thus exhibited the highest threshold voltage (Vth) in the voltage‐transmittance (V‐T) measurements for the minicells.

A Novel Soluble Azo Polyimide and Its Application As Liquid Crystal Photo-Alignment Layer

Novel Perylene Columnar Liquid Crystal Tuned by Azo Isomerization on Bay-Positions

Liquid-Crystal Photoalignment by Super Thin Azo Dye Layer

Synthesis and Characterization of A Novel Polyurethane-Based Photo-Alignment Layer Polymer for Liquid Crystal Displays

Polyimides with main-chain photosensitive groups: Synthesis, characterization and their properties as liquid crystal alignment layers

Soluble polyimide as liquid crystal perpendicular alignment layer

Ternary copolymerization photosensitive polyimide containing flexible group for liquid crystal alignment film

CINNAMATE_CONTAINING POLYIMIDE AND ITS FUNCTION AS LIQUID CRYSTAL PHOTOALIGNMENT LAYER

Novel Photoalignment Materials for Liquid Crystals Based on Modified Polysiloxane

Synthesis and Characterization of a Novel Mesomorphic Photoalignment Material for Liquid Crystals

Liquid Crystal Alignment on Polyimide Langmuir–Blodgett Films Prepared on a Newly Designed Langmuir Trough Using a Flowing Subphase

Liquid Crystal Alignment on Polyimide Langmuir-Blodgett Films

Alignment Modulation of Azobenzene-Containing Liquid Crystal Systems by Photochemical Reactions

Preparation and characterization of photo‐decomposable ester‐containing semi‐alicyclic polyimide alignment layers for potential applications in in‐plane switching thin‐film transistor liquid crystal display devices

A Nematic Liquid-Crystalline Polymer: Synthesis, Photoresponse and Optical Patterns

Recent Advances in Photoresponsive Liquid-Crystalline Polymers Containing Azobenzene Chromophores

Mesogen-co-polymerized Transparent Polyimide As a Liquid-Crystal Alignment Layer with Enhanced Anchoring Energy

Azobenzene Sulphonic Dye Photoalignment as a Means to Fabricate Liquid Crystalline Conjugated Polymer Chain‐Orientation‐Based Optical Structures

Polyimide Liquid Crystal Alignment Layers Prepared by Soft-Lithography

NONLINEAR OPTICAL AZO POLYIMIDE FROM POST-POLYMERIZATION AZO-COUPLING REACTION

Transfer of the in-plane molecular orientation of polyimide film surface to liquid crystal monolayer