Synthesis and Characterization of A Novel Polyurethane-Based Photo-Alignment Layer Polymer for Liquid Crystal Displays
HF Yu,HZ Jiang,YQ Lian,XG Wang,DS Liu
DOI: https://doi.org/10.3321/j.issn:0251-0790.2003.01.028
IF: 3.1
2003-01-01
Chemical Research in Chinese Universities
Abstract:A diol 1, 3-di (2-hydroxyethyl) 5-hydroxyl isoplithalate (DHHI) was synthesized through the nucleus substitution reaction of 5-hydroxyl isophthalic acid (HIA) The monomer was characterized by H-1-NMR, FTIR, elemental analysis and differential scanning calorimetry (DSC). Then a precursor polymer (PU-OH) containing hydroxyl groups was prepared by step polymerization of DHHI and. 4,4'-diphenylmethane-di-isocyanate (MDI). By PU-OH's functionalization with cinnamoyl chloride, a polyurethane (PU) with cinnamate side-groups (PU-CI) was obtained. The polymers synthesized were characterized with H-1-NMR, DSC, IR spectroscopy and elemental analysis. The photosensitive polymer PU-CI was found to be cross-linked under the irradiation of UV light through a cyclo [2 + 2] reaction. After processed by Linear Polarized Polymerization (LPP), the spin-coating films of PU-CI were changed into photo alignment layers. Then sandwich-type liquid crystal cells (LC cells) of a 50-mum-thick were assembled via a capillary action using nematic liquid crystal 5 CB. The microscopic photographs were obtained which showed the LC-aligning ability of PU-CI photo alignment layers. Therefore, the photosensitive polymer PU-CI synthesized has potential application as photo alignment layer in liquid crystal cells.