Abstract:To enhance the corrosion resistance, biocompatibility and mechanical durability of biomedical titanium alloys, a novel β-Ta2O5 nanoceramic coating was developed using a double glow discharge plasma technique. The surface morphology, phase composition and microstructure of the as-deposited coating were examined by atomic force microscopy (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The coating exhibits a striated structural pattern along the growth direction, which consists of equiaxed β-Ta2O5 grains, 15-20 nm in diameter in cross-section, showing a strong (001) preferred orientation. The mechanical properties and contact damage resistance of the β-Ta2O5 coating were evaluated by nanoindentation. Additionally, scratch tests were performed to evaluate the adhesion strength between the β-Ta2O5 coating and the Ti-6Al-4V substrate. The β-Ta2O5 coating shows high hardness combined with good resistance to both indentation and scratch damage, thus favoring it for long-term load-bearing application in the human body. Electrochemical behavior of the coating was analyzed in both a 0.9 wt % NaCl solution and Ringer's solution at 37 °C, by various electrochemical analytical techniques, including potentiodynamic polarization, electrochemical impedance spectroscopy, potential of zero charge and Mott-Schottky analysis. Compared with uncoated Ti-6Al-4V and commercially pure tantalum, the β-Ta2O5 coating possesses a more positive Ecorr and lower icorr in both aqueous solutions, which is attributed to the thicker and denser β-Ta2O5 coating that provides more effective protection against corrosive attack. In addition, the β-Ta2O5 coating shows stable impedance behavior over 5 days immersion under both simulated body solutions, corroborated by the capacitance and resistance values extracted from the EIS data. Mott-Schottky analysis reveals that the β-Ta2O5 coating shows n-type semiconductor behavior and its donor density is independent of immersion time in both aqueous solutions. Its donor density is of the order of 1 × 1019 cm-3, which is an order of magnitude less than that of the passive films formed on either commercially pure Ta or uncoated Ti-6Al-4V. Moreover, according to the differences between corrosion potential and potential of zero charge, the β-Ta2O5 coating exhibits a greater propensity to repulse chloride ions than both commercially pure Ta and uncoated Ti-6Al-4V. Therefore, the newly developed coating could be used to protect the surface of biomedical titanium alloys under harsh conditions.

Surface Composition and Corrosion Property of TiNi Alloys Coated with Tantalum Films

Surface Characteristics and Corrosion Resistance Properties of TiNi Shape Memory Alloy Coated with Ta

Surface characterization and immersion tests of TiNi alloy coated with Ta

Effects of Annealing Treatment on the Microstructure and Heamocompatibility of TiNi Alloys Coated with Ta

Surface Characterization of Thermally Oxidized Titanium Alloys

Research on the surface characterization, corrosion and bioactivity of nano-featured tantalum coating on selective electron beam melted Ti6Al4V alloy

Microstructure and Properties of Monolayer Ta and Multilayer Ta/Ti/Zr/Ta Coatings Deposited on Biomedical Ti-6Al-4V Alloy by Magnetron Sputtering

Tantalum coating inhibits Ni-migration from titanium out-diffusion in NiTi shape memory biomedical alloy

Plasma surface tantalum alloying on titanium and its corrosion behavior in sulfuric acid and hydrochloric acid

Study on microstructure and corrosion resistance of Ti-doped nickel-based alloy coatings

Tantalum Coated NiTi Alloy by PIIID for Biomedical Application

Corrosion properties of β-Ta alloyed Ti6Al4V by double-glow plasma surface alloying technique

Microstructure and properties of monolayer, bilayer and multilayer Ta2O5-based coatings on biomedical Ti-6Al-4V alloy by magnetron sputtering

Preparation of tantalum-containing coatings on NiTi shape memory alloys with enhanced in vitro cytocompatibility and antibacterial effectiveness

Mechanical, Electrochemical, and Osteoblastic Properties of Gradient Tantalum Coatings on Ti6Al4V by Prepared Plasma Alloying Technique

Surface Characterization and Electrochemical Studies of Biomedical Niti Alloy Coated with Tin by Piiid

Influence of sputtering atmosphere on the structural, biological, and electrochemical properties of tantalum-containing coatings on the NiTi alloy

Electrospark Deposition of Ti-Ta Coatings on Ti6Al4V Titanium Alloy: Oxidation Resistance and Wear Properties

Electrochemical Properties of a Novel Β-Ta2o5 Nanoceramic Coating Exposed to Simulated Body Solutions.

Microstructure, Wettability, Corrosion Resistance and Antibacterial Property of Cu-MTa2O5 Multilayer Composite Coatings with Different Cu Incorporation Contents

In vitro corrosion behavior of nano-multilayered TiN/Ti coated NiTi alloy