Performance of hybrid ceramic bearing at cryogenic and high-speed condition

古乐,王黎钦,齐毓霖,苏为民,钱宗德,郑亚青

DOI: https://doi.org/10.3321/j.issn:0367-6234.2004.02.007

2004-01-01

Abstract:To enhance the performances of cryogenic bearings operating in high speed under heavy load, hybrid bearings with silicon nitride ceramic balls are useed to replace the all-steel bearings with 9Cr18 stainless steel balls. The theoretical calculation and analyses of operating parameters for both hybrid and all-steel bearings at the d m · n value of 2. 14×106 mm · r/min and maximum contact press of 2 360 MPa are given. The results show that the centrifugal forces of balls in hybrid bearings are less than half of those in all-steel bearings, and their differences among all balls is very small while those change in a large range in all-steel bearings. The same trend is the differences of contact angles between ball and rings. The gyroscopic torque, spin-roll ratio in hybrid bearings and their range among balls are also smaller than those in all-steel bearings. The ball-to-disc tribological test between ball and ring materials without lubricant both in air and in liquid nitride show that the pair of silicon nitride ball and 9Cr18 stainless disc has steady friction coefficient and no severe adhesion while the pair of 9Cr18 stainless ball and 9Cr18 stainless disc display bad friction property and severe adhesions. The synthesis performance tests of hybrid bearings and all-steel bearings are conducted in liquid nitrogen on the high-speed bearing tester. The all-steel bearings endured less than 8 minutes while the hybrid bearings operated for more than 120 minutes.