Abstract:The effect of the reverse cyclic straining and the creep loading on the resultant tensile mechanical properties, such as the strength parameter (σ0.2 and σ b ), the ductile parameter (δ and ϕ f ) and the composite parameter of the strength and ductility, the static toughness (U t ), for the precipitation-strengthened nickel-based superalloy GH4145/SQ used for high-temperature turbine and valve studs/bolts in power plant was investigated systematically at a temperature of 538°C. The experimental results show that in the case of the reverse cyclic straining both σ0.2 and σ b increases at early stages of cyclic straining and, after reaching their saturated values, σ0.2 remains relatively constant until about 90% of fatigue life, while σ b exhibits continuous reduction up to a level equal to the maximum applied stress amplitude. With the increasing number of straining cycles, both δ and ϕ f as well as U t decrease significantly until final fracture. In the case of creep loading the strength parameters (σ0.2 and σ b ) tend to increase, as a whole, while the ductile parameters (δ and ϕ f ) and the static toughness (U t ) exhibit continuous decrease characterization as the amount of the creep deformation increases. The variation of the aforementioned various tensile mechanical properties during cyclic straining and creep loading of the alloy was further discussed by means of the observations of the deformation microstructures as well as the examinations of the fracture features of the specimens.

Time Dependent Failure Assessment Curves of 10crmo910 and 316 Stainless Steel

Evaluation of the time dependent failure assessment curves for 10CrMo910 and 316 SS at 550°C

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Time-dependent Failure Assessment Diagram for Integrity Assessment of Defective Structure at Elevated Temperature

A Modified Time-Dependent Failure Assessment Diagram for Cracks in Mismatched Welds at High Temperatures

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Creep Damage Analysis of 10crmo910 Steel

Safety assessment method for defective structures in creep regime

Constraint modified time dependent failure assessment diagram (TDFAD) based on <i>C</i>(<i>t</i>)-<i>A</i><sub>2</sub>(<i>t</i>) theory for creep crack

Integrity Assessment of Defected Structure at High Temperature with a Material Database

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Low Cycle Fatigue Damage Evolution & Life Estimate of 10CrMo910 Steel

Assessment of Creep Behavior Using a Damage-Coupled Model for Martensitic Stainless Steel

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

Creep fracture toughness of welded joint for 2.25Cr1Mo steel

TDFAD Approach to High Temperature Defect Assessment and Its Engineering Application

ON THE TIME-DEPENDENT MATERIAL FRACTURE TOUGHNESS AT HIGH TEMPERATURE

A Probabilistic Evaluation Method on Temperature and Time-Dependent Stress Intensity Limit St in Creep Assessment of Components at Elevated Temperatures

High -Temperature Creep Properties of Diffusion Bonding Joints of 316L Stainless Steel

Assessment of creep rupture properties for dissimilar steels welded joints between T92 and HR3C: CREEP PROPERTIES OF T92/HR3C WELDED JOINTS

Stress State Dependent Creep Damage Behavior of 9–12% Cr Steel Notched Components