Abstract:Commercially pure titanium specimens are subjected to three different treatments, and their bioactivity are evaluated by immersing the specimens in a simulated body fluid (SBF, Kokubo's recipe) for various periods up to 7 days, with particular attention being paid to the differences in apatite deposition between surfaces open to SBF and surfaces in contact with the container's bottom. The treatment with a H(2)O(2)/HCl solution at 80 degrees C for 30 min followed by heating at 400 degrees C for 1 h produces an anatase titania gel layer on the specimen surface. This gel layer deposits apatite both on the contact and on open surfaces, and apatite deposition ability does not change with pre-staking in distilled water. The treatment with a NaOH solution at 60 degrees C for 3 days produces a sodium titanate gel layer. This gel layer can deposit apatite only on the contact surface, and the apatite deposition ability is completely lost after 1 day of pre-staking in distilled water. It is concluded, therefore, that the bioactivity of the titania gel originates from the favorable structure of the gel itself while the bioactivity of the sodium titanate gel depends heavily on ion release from the gel. The third treatment, a simple heat treatment at 400 degrees C for 1 h, produces a dense (not porous) oxide layer on the specimen surface. The specimens can deposit apatite on the contact surface after only 3 days of staking in SBF, but they cannot deposit apatite on the open surface for up to 2 months of staking. The implications of such apatite deposition behavior have been discussed in relation to the environments of titanium implants in bone as well as to the methodology of the SBF staking experiment.

Preparation of bioactive titanium metal via anodic oxidation treatment in sulphate solution

Preparation of bioactive titanium metal via anodic oxidation treatment.

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Bioactive treatment of titanium surface using a H2O2/HCl solution

A Comparative Study of in Vitro Apatite Deposition on Heat-, H(2)O(2)-, and NaOH-treated Titanium Surfaces.

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution

Bioactive Titanium Metal Surfaces with Antimicrobial Properties Prepared by Anodic Oxidation Treatment

Preparation of Bioactive Tantalum Metal via Anodic Oxidation Treatment

In Vivo and In Vitro Studies on the Bioactivity of Anodic Oxidized Titanium Metal

[Preparation of Anodic Oxidation Layer on the Surface of Pure Titanium and Its Biological Activity Study].

PREPARATION OF BIOACTIVE FILM ON Ti6Al4V

Study on the Bioactivity of Anodic Oxidized Titanium Alloy Induced by Alkali Treatment

Surface potential change in bioactive titanium metal during the process of apatite formation in simulated body fluid

Enhanced Bioactivity of Chemically Oxidization-Modified Titanium Alloys

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

Nanostructured positively charged bioactive TiO2 layer formed on Ti metal by NaOH, acid and heat treatments

Bioactive Titanium Surfaces with the Effect of Inhibiting Biofilm Formation

Preparation, Characterization, in Vitro Bioactivity, and Osteoblast Adhesion of Multi-Level Porous Titania Layer on Titanium by Two-Step Anodization Treatment