Raw Material Synthesis and Single Crystal Growth of Yb∶KGW Laser Crystal

王英伟,程灏波,刘景和

DOI: https://doi.org/10.3969/j.issn.1000-985x.2004.06.003

2004-01-01

Abstract:The key factor for crystal growth of Yb∶KGW laser crystal is the selection of the flux and the design of the proper processes. Comparing the phase diagram and temperature field between K_2WO_4 and K_2W_2O_7, (Yb∶KGW) crystal was grown by the flux method using K_2W_2O_7 as a suitable flux. By analyzing the X-ray diffraction spectra of Yb∶KGW crystal powder sample and KGW powder sample, we found the same distribution of the diffraction maximum and the relative intensity, so it is concluded that the β-Yb∶KGW crystal is of low-temperature phase, monoclinic system and C2/c space group. On the basis of TG-DTA,the results show that Yb∶KGW has two obvious absorption peaks at 1086℃ and 1021℃ contrasting with the pure KGW crystal (melting point at 1031℃, phase transition temperature from tetragonal system to monoclinic system is 1088℃).The Yb∶KGW crystal's melting point is about 1086℃and the phase transition peak from tetragonal system to monoclinic is at 1021℃.