Crystal Gowth by Czochralski Method and Sectral Poperties of Yb3+:GdTaO4

Zhang Qingli,Zhou Wenlong,Liu Wenpeng,Ding Lihua,Luo Jianqiao,Yin Shaotang,Jiang Haihe

DOI: https://doi.org/10.3788/AOS20103003.0849

2010-01-01

Acta Optica Sinica

Abstract:Yb~(3+):GdTaO_4 was grown by Czochralski method.Its absorption,photoluminescence spectra were measured,and its spectral property parameters were computed.Full width at half maximum(FWHM) of absorption of Yb~(3+):GdTaO_4 is 56 nm,which is 2.4 times broader than that of Yb~(3+):YAG.Its absorption peaks are at 930,957 and 974 nm,whose absorption cross sections are 0.81×10~(-20),0.91×10~(-20),and 1.2×10~(-20) cm~2,respectively. The main peak of photoluminescence is at 1016 nm.The FWHM of emission peaking at 1016 and 1035 nm are 42 and 57 nm,which are 4～6 times wider than that of Yb~(3+):YAG,corresponding cross sections are 2.29×10~(-20) and 1.36×10~(-20) cm~2,respectively,which are a little higher than or equal to that of Yb~(3+):YAG.Its broad absorption band makes for decreasing the dependence on the temperature control of pump laser diode(LD),and broad emission band makes for realizing laser output of ultra-short pulse and tunable laser.Results indicate that Yb~(3+):GdTaO_4 is a very promising laser medium used in all-solid state ultra-short pulsed and tunable lasers.