The Transition of the Activation Energy of Semi-coke During Its Oxidation Process

张守玉,吕俊复,岳光溪,王洋

DOI: https://doi.org/10.3969/j.issn.1001-2060.2004.04.017

2004-01-01

Abstract:The activation energy of five kinds of semi-coke during its eigen oxidation in air was investigated by using a thermo-gravimetric balance. These semi-cokes were prepared from Datong coal, Shenmu coal, Yuxian coal, Jianjiang coal and Taiwan petroleum coke by pyrolysis for 7 minutes at a temperature of 900°C. A distributed activation energy model (DAEM) was employed to describe the transition of activation energy of semi-cokes during an oxidation process. Initially, the activation energy of Datong coal semi-coke assumes a minimum value. With an increase in carbon loss rate the activation energy will increase (the increase at initial period of reaction is relatively rapid), and decrease on reaching a peak value at a later period of reaction. The activation energy of Jianjiang coal semi-coke is very high at the initial period of reaction (as high as 250 kJ/mol). It decreases rather rapidly at first, but tends to decrease slowly when the carbon loss is assessed at 20%. As for the semi-coke of the other three kinds of coal their activation energy will experience respectively two peaks at the initial and later period of reaction with a relatively mild change between the two peaks. The different transition mechanisms of the activation energy specific to various kinds of semi-coke reflect their different internal qualities. As compared with coal cokes, the semi-coke of petroleum coke exhibits a relatively uniform internal structure.