Abstract:The microstructures and mechanical properties of Ti–Nb–V–Mo quaternary microalloyed high strength fire-resistant steel are investigated under different experimental conditions. The results show that the fire-resistant steel with high strength (ultimate tensile strength (UTS), 746 MPa; yield strength (YS), 597 MPa) and a low yield ratio (YS/UTS, 0.80) is successfully developed by rapid cooling combined with a low final cooling temperature. The microalloyed high strength fire-resistant steel tempered at 600 °C×15 min and 600 °C×180 min exhibit yield strength of 440 and 419 MPa, which values significantly exceed two-thirds of the specified yield strength at room temperature(i.e., 307 MPa) for the Q460 (YS ≥ 460 MPa) fire-resistant steel. The mechanical properties at room temperature and 600 °C even meet the requirements for the Q550 fire-resistant steel. The ferritic grain boundaries in the experimental steel tempered for 180 min at 600 °C show excellent stability. The analysis indicates that solid-solution strengthening and precipitation strengthening are important in improving the strength of the studied fire-resistant steel at room temperature and 600 °C, respectively. M(C, N) (M=Nb, V, Ti, and Mo) and M3C (M=Fe, Cr, Mn, and Mo) particles in small quantities are found in the matrix of the as-rolled sample. However, after reheating and tempering at 600 °C, large amounts of M(C, N) (mainly MC) and M3C particles precipitate. With an increasing in tempering time, the amount of nanoscale MC precipitate increases; especially, the amount of the MC particles size smaller than 10 nm, and the mass fraction of Nb, V, and Mo in the MC precipitate also increases, which is consistent with the equilibrium thermodynamic calculation results. This enhancement of the precipitation strengthening of secondary phase particles compensates for strength loss attributing to a decrease in shear elastic modulus and solid solution strengthening at 600 °C.

Behavior of Alloying Elements in Precipitation-Hardening Hot Work Steel

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Effect of cobalt on precipitation in Fe-Cr-Co-Mo-Ni-C stainless steels

Electron Theory Study on Mechanism of Action of Cobalt in Fe-Co-Cr Based High-Alloy Steel

Microstructures and Mechanical Properties of a L12-structured Precipitation Strengthened Co-based Superalloy

Effects of Alloying Elements on the Microstructure of Precipitation Strengthened Co-based Superalloys

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Carbide Precipitation Behavior of High‐Alloy Steel During Solidification and Cooling Process

High-Temperature Mechanical Behavior of Cobalt-Free FeMnCrNi(Al) High-Entropy Alloys

Precipitation Law of Vanadium in Microalloyed Steel and Its Performance Influencing Factors

Effect of V on the Precipitation Behavior of Ti−Mo Microalloyed High-Strength Steel

Influence of V on the Microstructure and Precipitation Behavior of High-Carbon Hardline Steel during Continuous Cooling

Influence of Alloying Elements on the Dynamic Recrystallization of 4 wt.-% Medium Manganese Steels

Effect of precipitation-induced element partitioning during tempering on mechanical properties of hot-rolled 3Mn steel after intercritical annealing

Precipitation behavior of Ti–Nb–V–Mo quaternary microalloyed high strength fire-resistant steel and its influence on mechanical properties

Secondary Phase Precipitation in Fe-22Mn-9Al-0.6C Low-Density Steel during Continuous Cooling Process

Improved Red Hardness and Toughness of Hot Work Die Steel through Tungsten Alloying

Strengthening of Ni-Mn-Cu-Al-Co steel by nanoscale Cu and β-NiAl co-precipitated couples

Effect of annealing temperature on carbide precipitation, microstructure and mechanical properties of Fe-Mn-C- (Cr, Mo, W, Ni, Nb, Ti, V) multi-alloying TWIP steel

Study on Diversified Carbide Precipitation in High‐Strength Low‐Alloy Steel during Tempering

Effect of alloying elements on the coarsening rate of γʹ precipitates in multi-component CoNi-based superalloys with high Cr content