A green-yellow phosphor Mg1.94-xAl3.96Si5.04O18: 0.06Ce3+, xTb3+ with thermal anti-quenching property
Xiao-gang Zhang,Cong Zhao,Shi-xiu Cao,Li-chun Dong,Lei Liu,Yang Liu,Jiang-kun Li,Jun Wang
DOI: https://doi.org/10.1016/j.ijleo.2020.164809
IF: 3.1
2020-09-01
Optik
Abstract:Ce3+/Tb3+ co-doped phosphors Mg1.94-xAl3.96Si5.04O18: 0.06Ce3+, xTb3+ were prepared by using high temperature solid-state reaction method. The crystal structure, photoluminescence spectrum, decay time and thermal stability of the obtained samples were systematically investigated. The CIE chromaticity coordinates dramatically shifted from (blue region, 0.1518, 0.0972) to (green-yellow, 0.2537, 0.5428) with the increasing of the Tb3+ concentration. The emission spectra shown that the optimum concentration of Tb3+is 0.03 mol in the Mg1.94-xAl3.96Si5.04O18: 0.06Ce3+, xTb3+ phosphors. The sample of x =0.03 mol emitted a green-yellow light under the excitation of near-ultraviolet light ∼ 330 nm. The critical distance between the co-doped ions is calculated to be ∼ 15.99 Å. The energy transfer type from Ce3+ to Tb3+ was determined dipole-dipole interaction. The energy transfer efficiency between the Ce3+ and Tb3+ in Mg1.94-xAl3.96Si5.04O18: 0.06Ce3+, 0.03Tb3+ was calculated to be 84.23 %, which indicated the energy transfer with a high efficiency. Moreover, the emission intensity of the sample (x = 0.03) increased with the increasing of environmental temperature, which indicated that the sample has thermal anti-quenching property. The obtained results implied that the as-prepared phosphor material has a potential application for near-ultraviolet white LEDs.
optics