Abstract:Rare earth aluminate phosphors are well-known for being nontoxic and environmentally friendly. In this work, Tb3+-doped SrLaAlO4 phosphors were synthesized via a facile high temperature solid-state reaction method. The Optimum reaction temperature is determined to be 1300 degrees C based on the results of powder X-ray diffraction (XRD). The SEM patterns and TEM images correspond with the results of Rietveld refinement and show that the SrLa1-xAlO4:xTb(3+) samples present a flaky structure. The results of photoluminescence spectrums (PL) show that SrLa1-xAlO4:xTb(3+) phosphors can absorb in the UV-vis spectral region of 228 nm-263 nm and exhibit several emission peaks between 450 and 650 run, and the highest peak was at 508 nm. The luminescence properties of SrLa1-xAlO4:xTb(3+) have a strict dependence on the cation substitution levels. When the doping concentration of Tb3+ was 0.05, the emission intensity of the sample is strongest. The thermal quenching result of the SrLa0.95AlO4:xTb(3+) phosphors shows that these phosphors are relatively sensitive to temperature changes under an excitation of 228 nm, as the temperature increases from 25 degrees C to 125 degrees C, the emission intensity (peak at 548 nm) decayed to 55.11% of that at room temperature. However, when the temperature increases to 125 degrees C, the emission intensity (peak at 548 nm) decayed to 61.16% of the initial value under an excitation of 263 nm, which showed a relatively good thermal stability. The internal quantum efficiency (QE) values of the SrLa0.95AlO4:xTb(3+) phosphors was measured and determined to be 48%. Under excitations of 228 nm and 263 nm, the lifetimes of the optimized sample SrLa0.95AlO4:xTb(3+) were 1.3986 ms and 1.2095 ms, respectively, and the CIE coordinates of the sample were calculated as (0.2971, 0.4981), (0.3056, 0.5329), respectively. Under both excitations SrLa0.95AlO4:xTb(3+) exhibited high-color-purity green emission.

Co-Precipitation Synthesis and Photoluminescence Properties of Ce3+ Activated Terbium Aluminum Garnet (Tb1-Xcex)(3)al5o12 (0 <= X <= 0.05) Yellow Phosphors

Co-Precipitation Synthesis and Photoluminescence Properties of Ce<sup>3+</sup> Activated Terbium Aluminum Garnet (Tb<sub>1<i>-x</i></sub>Ce<sub><i>x</i></sub>)<sub>3</sub>Al<sub>5</sub>O<sub>12</sub> (0≤<i>x≤</i>0.05) Yellow Phosphors

Yellow-emitting (tb 1−x Ce X ) 3 Al 5 O 12 Phosphor Powder and Ceramic (0≤x≤0.05): Phase Evolution, Photoluminescence, and the Process of Energy Transfer

Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process

The Effects of Ga3+ Substitution on Local Structure and Photoluminescence of Tb3Al5O12:Ce Garnet Phosphor

Synthesis and photoluminescence properties of cerium-doped terbium–yttrium aluminum garnet phosphor for white light-emitting diodes applications

Synthesis and Photoluminescence Properties of Tunable Green-Orange Cerium-Doped Terbium-Lutetium Aluminum Garnet

Tunable luminescence Y3Al5O12:0.06Ce 3+, xMn2+ phosphors with different charge compensators for warm white light emitting diodes

A green-yellow phosphor Mg1.94-xAl3.96Si5.04O18: 0.06Ce3+, xTb3+ with thermal anti-quenching property

Synthesis and luminescent properties of (Ce0.67-xGdxTb0.33) MgAl11O19 phosphors

Tunable luminescence Y_3Al_5O_12:006Ce^3+, xMn^2+ phosphors with different charge compensators for warm white light emitting diodes

Luminescence Properties And Energy Transfer Of Ce3+,Tb3+-Coactivated-Sialon Phosphors

Luminescence Properties of Ce3+ Doped Garnet Ca2LaZr2Al3O12 Phosphors

Synthesis and Characterization of (Ce0.67tb0.33)mnxmg1-Xal11o19 Phosphors Derived by Sol-Gel Processing

Preparation, Structure, Luminescence Properties of Terbium Doped Perovskite-Like Structure Green-Emitting Phosphors SrLaAlO4:Tb3+

Processing and valence-dependent photoluminescence of (Tb1-xEux)3Al5O12 garnet phosphors (x=0.0025–0.05)

Photoluminescence properties, excellent thermal stability and energy transfer in Ce3+ and Tb3+ co-doped Sr3Gd2(BO3)4 phosphors

Photoluminescence and Thermoluminescence of Ce3+ Incorporated Y3Al5O12 Synthesized by Rapid Combustion

Luminescence Properties of Color Tunable New Garnet Structure (Lu1-Xmnx)3al2(al1-xsix)3o12: Ce3+ Solid Solution Phosphors

Microstructure and Luminescence Characteristics of YxAl5O12∶Ce3+Phosphor

Emitting-Color Tunable Phosphors Sr3gao4f:Ce3+ At Ultraviolet Light And Low-Voltage Electron Beam Excitation