High temperature gaseous rare-earth permeation of polyoxotungstates: An new effective method for the preparation of tungsten bronzes

Zhonghua Li,YongDe Wei,Yuanru Guo,Baibin Zhou,李中华,韦永德,郭元茹,周百斌
IF: 4.632
2004-01-01
Journal of Rare Earths
Abstract:New polyoxometalate alpha-K12H3[Y(BW11O39)(2)](.)25H(2)O was synthesized and treated by high temperature gaseous rare earth permeation to prepare tungsten bronze K0.475WO3. XRD, TG-DTA, XPS, W-183-NMR, CV and AC impedance spectra were used to characterize the resulting material. The results of XPS indicate that La has permeated and diffused into the body of the sample and exists in the forms of binding with other components. The crystal structure parameters of K0.475WO3 were obtained by the analysis of XRD, which shows tetragonal crystal system with lattice parameters: a = 12.28 nm, c = 3.833 nm, V = 578.48 nm(-3). The conductivities calculated from the results of AC impedance spectra of the material increase with the increasing of temperature, which shows a semiconductor character.
What problem does this paper attempt to address?