Abstract:Tungsten oxide (WO3) nanoparticles with monoclinic structure have been synthesized by using an inexpensive coprecipitation process. The obtained nanoparticles were annealed at 400°C, 500°C, 600°C, 700°C, 800°C, and 900°C for 1 h under the same physical conditions. The morphology, structure, and optical properties of the synthesized nanoparticles were studied by x-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), ultraviolet–visible (UV–Vis) spectrophotometry, and Raman spectroscopy. The XRD results confirmed that the synthesized nanomaterial was crystalline in nature with monoclinic phase. The crystallite size varied from 14 nm to 87 nm when changing the annealing temperature. Williamson–Hall analysis was used to investigate the change in lattice strain and crystallite size. The optical performance was investigated by using UV–visible spectroscopy. The bandgap of the prepared nanomaterials varied from 2.51 eV to 3.77 eV with the annealing temperature, due to the variation of the effect of oxygen vacancies on the electronic band structure. SEM revealed formation of uniform and irregular-sized nanoparticles. HRTEM analysis revealed that the nanoparticles grew along the [002] plane with d-spacing of 0.39 nm for the material annealed at 500°C and along the [200] plane with spacing of 0.36 nm when annealed at 800°C. The crystalline nature of the synthesized nanomaterial was confirmed by uniform and clear fringes obtained in TEM micrographs. The correlation between the peak position and width of the key band at 806 cm−1 in Raman spectroscopy band is discussed. These enhancements in the properties of WO3 nanomaterial make it an efficient material for many potential applications, e.g., in photocatalysis, electro- and photochromic devices, etc.

Hydrothermal Synthesis and Photochromism Property of Superfine Powders of Metastable Tungsten Oxide

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

Atomic Scale Stability of Tungsten-Cobalt Intermetallic Nanocrystals in Reactive Environment at High Temperature.

Hydrothermal Synthesis and Photoluminescence of Hierarchical Lead Tungstate Superstructures: Effects of Reaction Temperature and Surfactants

Synthesis of Tungsten Oxide Nanoparticles using a Hydrothermal Method at Ambient Pressure

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Synthesis and Photochromism Property of Colloidal and Films of Tungsten Bronze

Synthesis of Tungsten Trioxide and Lithiated Tungsten Oxides by a Soft Chemistry Route and Their Structural Stability

Electrostatic-Induced Synthesis Of Tungsten Bronze Nanostructures With Excellent Photo-To-Thermal Conversion Behavior

Mechanochemical synthesis of sodium tungsten bronze nanocrystalline powders

Novel synthesis of hexagonal WO3 nanostructures

Preparation and Thermochromic Property of Tungsten-Doped Vanadium Dioxide Particles

Hydrothermal Synthesis and Effects of Ph Values on Properties of CdWO4 Powders

Synthesis of Pyrochlore Tungsten Trioxide Thin Film and Electrochemical Lithium Intercalation

Synthesis and Applications of Γ-Tungsten Oxide Hierarchical Nanostructures

Sol-gel synthesis and characterization of tungsten-molybdenum solid solution nanoparticles

Chemical synthesis and electronic conduction properties of sodium and potassium tungsten bronzes

Effect of Annealing on the Surface Morphology, Optical and and Structural Properties of Nanodimensional Tungsten Oxide Prepared by Coprecipitation Technique

Conditions and Mechanism of Crystallization of Hydrous W-Fe Oxides with a Pyrochlore-Type of Structure (Elsmoreite Group) in the Oxidation Zone of Ore Deposits

Structural phase transition of tungsten-doped vanadium dioxide nanopowders prepared by thermolysis

Sustainable and green synthesis of hydrogen tungsten bronze nanoparticles with nanocarbon via mechanically induced hydrogen spillover