Synthesis and Performance of LiMnPO4 Used As Cathode Material for Lithium Ion Batteries

XY Chang,ZX Wang,XH Li,Q Kuang,WJ Peng,HJ Guo,YH Zhang

DOI: https://doi.org/10.3866/pku.whxb20041017

2004-01-01

Abstract:Olivine LiMnPO4 was synthesized at 600 degreesC and 800 degreesC by the method of solid-state reaction combining with the addition of carbon black and ball-milling of reagents and precursors. Structure, surface morphology and charge/discharge performance of LiMnPO4 Were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical measurement, respectively. Sample synthesized at 600 degreesC by ball-milling of reagents for 24 h and precursors for 12 h contains impurities and large, densely sintered blocks. Pure olivine LiMnPO4 with large particle size is obtained at 800degreesC by the same ball-milling process. It is shown that these materials can't charge or discharge effectively in the electrochemical tests. On the contrary, sample prepared at 600degreesC by ball-milling of reagents for 36 h and precursors for 24 h presents pure phase with small and almost identical particles size (about 100 similar to 200 nm). The initial discharge capacity of this sample is approximately 100 mAh . g(-1). Mixing of the agents and the precursors and the choice of sintering temperature are two important factors to obtain pure olivine LiMnPO4 with reversible charge-discharge capacity.