Study On The Nano-Cuo Powder Made From The Precursor Synthesized By The Precipitation Method In Mixed Solvent

Dongsheng Li,Wenliang Wang,Yaoyu Wang,JiWu Wang,Qizhen Shi
DOI: https://doi.org/10.3321/j.issn:1001-4861.2004.05.025
2004-01-01
Chinese journal of inorganic chemistry
Abstract:Nano-CuO was prepared by heating nano-Cu-2(OH)(2)CO3 precursors in different calcination temperatures.. The precursor was synthesized from water-alcohol mixed solution of Cu (Ac)(2) using mixed solution of NaOH and Na2CO3 as precipitants. XRD, FT-IR, TEM, TG-DTA and surface area measurement techniques were used to investigate the properties of the CuO powder. The results show that the spherical, well dispersed nano-CuO powder with the average size of 15 nm and higher catalytic activity for H2O2 decomposition was obtained at 300 degreesC. With the increasing of calcination temperature, crystal of CuO grows up, agglomeration of the powder becomes heavier and catalytic activity decreases. FF-IR patterns revealed that the vibration fine structure of Cu-O bond in nano-CuO powder disappears and main absorption is red-shifted with the average size of nano-CuO reducing.
What problem does this paper attempt to address?