Improving the Photostability and Water Resistance Stability of Chalcogenide Red Phosphor with Inert CaF2 Shells
Meng Tian,Hong Wang,Xiumei Yin,Ke Cai,Jianxin Jiao,Qiang Pang,Yao Fu,Mingming Xing,Kaiying Liu,Ying Tian,Xixian Luo
DOI: https://doi.org/10.1016/j.colsurfa.2021.127678
2021-01-01
Abstract:(Ca,Sr)S:Eu2+ as an important commercial red phosphor has been widely used in our daily life. However, (Ca,Sr) S:Eu2+ is extremely sensitive to moisture and ultraviolet (UV) light, which severely limits its service life and wide applications. Here epitaxial growth of dense CaF2 shell on the surface of (Ca,Sr)S:Eu2+ particles is successfully achieved by a liquid-phase thermal decomposition method. The red emission of the (Ca,Sr)S:Eu2+ phosphor is increased as much as 40% after coating with a CaF2 shell. This is attributed to the effective protection of luminescent center of Eu2+ ions in the core from surface quenching. Moreover, after continuous exposure to intense sunlight in air for 9 days, no luminescence degradation is observed for the (Ca,Sr)S:Eu2+@CaF2 sample, while the red emission of the (Ca,Sr)S:Eu2+ phosphor is severely quenched by 66%. The water resistance experiments show that the dense shell of CaF2 can protect the crystal structure of (Ca,Sr)S by suppressing the hydrolysis reaction. The red emission of the (Ca,Sr)S:Eu2+@CaF2 sample after being fully soaked in water for 30 min is comparable to that of the original (Ca,Sr)S:Eu2+ phosphors. Our results provide a new and versatile avenue to improve the stabilities of chalcogenide phosphors, thus making them attractive for wide applications.