Abstract:Ce-modified Mn-Fe mixed-oxide catalysts were prepared by a citric acid sol-gel method and characterized by X-ray diffraction, Raman, N-2 adsorption-desorption, infrared spectra, H-2 temperature-programmed reduction and thermogravimetric analyses. Their catalytic properties were investigated in ozone (O-3) decomposition reaction. Results show that the small amount of rare earth metal Ce added during Mn-Fe (FM) mixed-oxide synthesis greatly improves the catalytic performance in O-3 decomposition. Among the prepared catalysts, the C-0.04(FM)(0.96) mixed-oxide catalyst exhibits the highest catalytic activity and stability. The O-3 conversion over C-0.04(FM)(0.96 )is 98% after 24 h reaction at 25 degrees C under dry condition, and that over FM decreases to 90% after 16 h reaction. At 0 degrees C, the O-3 conversion over Ca-0.04(FM)(0.96) is 95% after 7 h reaction under dry condition, and that over FM slows down to 70%. Under humid condition (RH = 65%), the O-3 conversion over C-0.04(FM)(0.96) is 63% after 6.5 h reaction at 25 degrees C, while that over FM decreases to 55%. When Ce is doped into Mn-Fe mixed oxides, the small amount of Ce enters the crystal lattice of MnO2, and partial Fe is separated to form Fe2O3. This changes cause lattice distortion and increase defects and enable the as-synthesized Ce-Fe-Mn ternary mixed-oxide catalysts to acquire additional oxygen vacancies and increase their specific surface area, thereby increasing the number of reaction sites and enhancing the catalytic performance of the catalysts for O-3 decomposition. (C) 2020 Published by Elsevier B.V. on behalf of Chinese Society of Rare Earths.

Catalysts for decomposing ozone tail gas.

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Removal of Dilute VOCs in Air by Post-Plasma Catalysis over Ag-based Composite Oxide Catalysts

Catalytic Ozonation of Toluene over Spinel Cumn2o4: Influencing Factors, Reaction Mechanism and Pathways

Effect of ambient factors over spinel CuMn2O4 for toluene catalytic ozonation: Enhancement of the synergy and the generation of ROS

Ozone Assisted Oxidation of Gaseous PCDD/Fs over CNTs-containing Composite Catalysts at Low Temperature.

Ce–Fe–Mn Ternary Mixed-Oxide Catalysts for Catalytic Decomposition of Ozone at Ambient Temperatures

Catalytic Decomposition of Airborne Ozone by MnCO3 and Its Mechanism

Preparation of zinc oxide catalyst with activated carbon support for ozone decomposition

Regeneration of Ozone Decomposition Catalysts by Elimination of O2 2 2- from Oxygen Vacancies

Regeneration of Ozone Decomposition Catalysts by Elimination of O22- from Oxygen Vacancies

Catalytic Decomposition of Low Level Ozone with Gold Nanoparticles Supported on Activated Carbon

Ethanol-thermal synthesis of colloidal-CeFeMn mixed-oxide as efficient catalytic material for atmospheric ozone decomposition

Removing Surface Hydroxyl Groups of Ce-Modified MnO2 to Significantly Improve Its Stability for Gaseous Ozone Decomposition

Catalytic Decomposition of Residual Ozone over Cactus-like MnO2 Nanosphere: Synergistic Mechanism and SO2/H2O Interference

Catalytic Ozone Aqueous Decomposition of Methylene Blue Using Composite Metal Oxides

Synthetic effect of supports in Cu-Mn–doped oxide catalysts for promoting ozone decomposition under humid environment

Catalytic Decomposition of Residual Ozone over Cactus-like MnO 2 Nanosphere: Synergistic Mechanism and SO 2 /H 2 O Interference

Catalytic Decomposition of Low-Level Ozone by Au/Ac Prepared by A Sol Immobilization Method

Synthesis of Highly Porous Cu2O Catalysts for Efficient Ozone Decomposition

Exceptional Ozone Decomposition over -MnO2/AC under an Entire Humidity Environment