Abstract:A series of V-Ce(SO4)(2)/Ti catalysts for selective catalytic reduction (SCR) of NO with ammonia are prepared by impregnation method. Low temperature SCR activity and alkali resistance of the optimal V-0.5Ce(SO4)(2)/Ti sample are found to be better than on the commercial V-W/Ti catalyst. Also, V-0.5Ce(SO4)(2)/Ti shows an excellent durability in the presence of SO2 and H2O, indicating to have prospects for the industrial application. Based on catalysts characterization and in-situ DRIFTS studies, a higher proportion of surface active oxygen generated by the introduction of Ce and a Much faster H-2 reduction point out the improved redox properties of V-0.5Ce(SO4)(2)/Ti, which results in a stronger NO oxidative activation and is confirmed by a more abundant formation of surface NO and NO3-species. When exposed to SCR conditions where both NH3 and NO are present, this enhanced NO activation can produce more reactive nitrite and/or NO+ intermediates which then readily react with adsorbed NH3 and decorripose to N-2 and H2O, accounting for the improved SCR activity of V-0.5Ce(SO4)(2)/Ti at low temperatures. The addition of Ce(SO4)(2) also provides abundant reactive acid sites and adsorbed NH3 species thus increase. Even after Na poisoning, adequate surface acidity and redox properties still remain. Furthermore, relatively higher contents of V-OH are preserved owing to the interaction between Na and O=S=O, acting as a protection for the active sites. These promotional effects contribute to the better alkali resistance of V-0.5Ce(SO4)(2)/Ti. Therefore, all the results suggest that V-0.5Ce(SO4)(2)/Ti is a promising candidate as a catalyst for NH3-SCR in coal-fired power plants, especially under high Na-content conditions. (C) 2017 Elsevier B.V. All rights reserved.

Catalytic performance of a novel ceramic-supported vanadium oxide catalyst for NO reduction with NH3

[Catalytic Performance of a Novel Ceramic-Supported Vanadium Oxide Catalyst for NO Reduction with NH3].

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Selective catalytic reduction of NO with NH3 over wire-mesh honeycomb supported V2O5-MoO3/TiO 2/Al2O3 catalyst

Performance of V_2O_5-WO_3-MoO_3/TiO_2 Catalyst for Selective Catalytic Reduction of NO_x by NH_3

SO2 Promoted V2O5-MoO3/TiO2 Catalyst for NH3-SCR of NOx at Low Temperatures

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Nh3 Selective Catalytic Reduction of No: A Large Surface Tio2 Support and Its Promotion of V2o5 Dispersion on the Prepared Catalyst

Selective catalytic reduction of NOx with NH3 over V2O5-WO3/TiO2-ZrO2 monolith catalysts

Selective Catalytic Removal of High Concentrations of NOx at Low Temperature

Washcoating of cordierite honeycomb with vanadia–tungsta–titania mixed oxides for selective catalytic reduction of NO with NH3

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

Experimental Study on Preparation of V_2O_5-WO_3-MoO_3/TiO_2 Catalysts and Selective Reduction of NO_x with NH_3

Catalytic Performance and Kinetics of Wire-Mesh Honeycomb Catalyst for Reduction of NO with NH3.

V2O5-WO3/TiO2 Catalysts for Low Temperature NH3 SCR: Catalytic Activity and Characterization

Performance of V2o5-Wo3-Moo3/Tio2 Catalyst for Selective Catalytic Reduction of Nox by Nh3

Comparative Study on V-W/TiO2/γ-Al2O3 for Selective Catalytic Reduction of NO

Active Vanadium(IV) Species Synthesized at Low-Temperature Facilitate Excellent Performance in Low-Temperature NOx-Catalytic Removal

Catalytic Activity of SiO2 Doped V2 O5/WO3-TiO2 for Selective Catalytic Reduction of NOx by NH3

Effects of MoO on Dispersion of Vanadia and Low-Temperature NH3-SCR Activity of Titania Supported Catalysts: Liquid Acidity and Steric Hindrance

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3