Experiment and Analysis of Uniaxial Tensile Mechanical Properties of ECTFE Foils Under Different Strain Rates
Wujun Chen,Changjiang Liu,Bing Zhao
DOI: https://doi.org/10.11784/tdxbz201904077
2019-01-01
Abstract:Uniaxial tensile tests of ethylene-chlorotrifluoroethylene(ECTFE)foils were conducted in this paper. ECTFE foils with a thickness of 250μm were used. The dumbbell-shaped specimens were manufactured according to the machine direction(MD)and the transverse direction(TD)of the foils. The stress-strain curves of the foils were obtained under eight constant strain rates(0.02,0.20,0.50,1.00,2.00,4.00,6.00,and 10.00 min-1). Based on the stress-strain curves,tensile strength,tensile strain at break,yield stress,yield strain,and elastic modulus were analyzed and calculated. Based on the test results and analysis,some useful findings could be derived. The uni-axial tensile mechanical properties of the ECTFE foils along the MD and TD directions were almost identical. The stress-strain curves showed obvious nonlinearity,in which there were four main stages of linear elasticity,strain softening,cold tension,and strain hardening from the beginning of tension to fracture. Main mechanical parameters such as modulus of elasticity,yield strength,tensile strength,and elongation at break showed nonlinear exponential relation with the strain rate. The nonlinear fitting formulas are also given,which can be used to predict the mechani-cal parameters of ECTFE foils under different strain rates.