LANTHANUM TITANATE NANOPARTICLES ER FLUIDS WITH HIGH PERFORMANCE
De Wang,Rong Shen,Shiqiang Wei,Kunquan Lu
DOI: https://doi.org/10.1142/9789814340236_0037
2011-01-01
Abstract:Electro-Rheological Fluids and Magneto-Rheological Suspensions, pp. 266-271 (2011) No AccessLANTHANUM TITANATE NANOPARTICLES ER FLUIDS WITH HIGH PERFORMANCEDE WANG, RONG SHEN, SHIQIANG WEI, and KUNQUAN LUDE WANGBeijing National Laboratory for Condensed Matter Physics and Key Laboratory of Soft Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, ChinaNational Synchrotron Radiation Laboratory, University of Science and Technology of China, Hefei 230029, China, RONG SHENBeijing National Laboratory for Condensed Matter Physics and Key Laboratory of Soft Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China, SHIQIANG WEINational Synchrotron Radiation Laboratory, University of Science and Technology of China, Hefei 230029, China, and KUNQUAN LUBeijing National Laboratory for Condensed Matter Physics and Key Laboratory of Soft Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, Chinahttps://doi.org/10.1142/9789814340236_0037Cited by:0 (Source: Crossref) PreviousNext AboutSectionsPDF/EPUB ToolsAdd to favoritesDownload CitationsTrack CitationsRecommend to Library ShareShare onFacebookTwitterLinked InRedditEmail Abstract: A new type of electrorheological (ER) fluid consisting of lanthanum titanate (LTO) nanoparticles is developed. The ER Fluids were prepared by suspending LTO powder in silicon oil and the particles are fabricated by wet chemical method. This ER fluid shows excellent ER properties: The static yield stress reaches over 150kPa under 5kV/mm with linear dependence on the applied DC electric field, and the current density is below 10μA/cm2. In order to investigate the affect factor on the ER behavior the LTO powder were heated under different temperatures. The ER performances of both two particles treated under different temperatures were compared and the properties of those particles were analyzed with TG-FTIR technique. It was found that the static yield stress of the suspensions fell from over 150kPa to about 40kPa and the current densities decreased prominently as the rise of the heating temperature. TG-FTIR analysis indicated that organic groups remained in the particles such as alkyl group, hydroxyl group and carbonyl group and etc, may contribute to the ER effect significantly. The experimental results are helpful to understand the mechanism of the high ER effect and synthesize better ER material. This work is supported by the National Natural Science Foundation of China Grant 10674156, the National Basic Research Program of China Grant 2004CB619005 and 2009CB930800, the Knowledge Innovation Project of Chinese Academy of Sciences Grant KJCX2-YW-M07, and the Instrument Developing Project of the Chinese Academy of Sciences, Grant No. YZ200758. FiguresReferencesRelatedDetails Recommended Electro-Rheological Fluids and Magneto-Rheological SuspensionsMetrics History PDF download