Phase-Controlled Synthesis of High-Bi-Ratio Ternary Sulfide Nanocrystals of Cu1.57Bi4.57S8 and Cu2.93Bi4.89S9
Xiaoru Ren,Long Yuan,Qingshuang Liang,Renguo Xie,Zhibin Geng,Yu Sun,Lei Wang,Keke Huang,Tianli Wu,Shouhua Feng
DOI: https://doi.org/10.1002/cplu.201800271
2018-01-01
ChemPlusChem
Abstract:High Bi-ratio ternary sulfides have been recently reported as superior thermoelectric materials. However, the synthesis of high Bi-ratio Cu-Bi-S nanocrystal remains a challenge. Reported here are the synthesis and characterization of three-phase Cu-Bi-S nanocrystals with the nominal chemical formulae of Cu1.57Bi4.57S8, Cu2.93Bi4.89S9 and Cu3BiS3. The samples were prepared using a Bi2S3 precursor by varying the amount and type of Cu2-xS (i.e. Cu2S or Cu7.2S4) reactants. TEM images reveal that two new samples crystalized having nanorod morphology with radii of approximately 50nm and lengths of 200nm. XPS results indicate that the valence states of Bi in both the two new phases are +3 with viable oxidation states for Cu. UV-Vis-NIR absorption spectroscopy reveals that narrow direct bandgaps are 1.12 and 1.27eV for Cu1.57Bi4.57S8 and Cu2.93Bi4.89S9, respectively. Besides, this method could also be applied to synthesize the Cu3BiS3 phase with a new nanoplate morphology. The as-synthesized Cu-Bi-S samples show Cu/Bi ratio-dependent photoresponsive properties. This study not only reports the structure and bandgap of two ternary sulfides, which have only been discovered in the mineral previously, but also provides an efficient method for synthesizing Bi-rich ternary chalcogenide nanocrystals.